| Physical Properties | Metric | English | Comments |
|---|---|---|---|
| Base Resin Density | 0.918 g/cc | 0.0332 lb/in3 | ASTM D1505 |
| Base Resin Melt Index | 3.5 g/10 min | 3.5 g/10 min | I2; ASTM D1238 |
| Mechanical Properties | Metric | English | Comments |
| Film Elongation at Break, MD | 510 % | 510 % | ASTM D882 |
| Film Elongation at Break, TD | 680 % | 680 % | ASTM D882 |
| Elmendorf Tear Strength, MD | 10.0 g/micron | 254 g/mil | ASTM D1922 |
| Elmendorf Tear Strength, TD | 25.0 g/micron | 635 g/mil | ASTM D1922 |
| Dart Drop | 7.00 g/micron | 178 g/mil | ASTM D1709A |
| Film Tensile Strength at Break, MD | 73.5 MPa | 10700 psi | ASTM D882 |
| Film Tensile Strength at Break, TD | 46.1 MPa | 6690 psi | ASTM D882 |
| 1% Secant Modulus, MD | 117.68 MPa | 17068 psi | ASTM D882 |
| 1% Secant Modulus, TD | 137.30 MPa | 19913 psi | ASTM D882 |
| Optical Properties | Metric | English | Comments |
| Haze | 2.4 % | 2.4 % | ASTM D1003 |
| Gloss | 86 % | 86 % | 45°; ASTM D2457 |
| Processing Properties | Metric | English | Comments |
| Melt Temperature | 250 - 310 °C | 482 - 590 °F | |