- 拉伸強(qiáng)度 [MPa]: 11.8
- 脆化溫度 [℃]: -70.0
| Physical Properties | Metric | English | Comments |
|---|---|---|---|
| Base Resin Density | 0.918 g/cc | 0.0332 lb/in3 | ASTM D1505 |
| ESCR 100% Igepal? | 150 hour @Thickness 3.80 mm, Temperature 23.0 °C | 150 hour @Thickness 0.150 in, Temperature 73.4 °F | slit; ASTM D1693 |
| Base Resin Melt Index | 25 g/10 min | 25 g/10 min | I2; ASTM D1238 |
| Mechanical Properties | Metric | English | Comments |
| Tensile Strength at Break | 8.83 MPa | 1280 psi | ASTM D638 |
| Tensile Strength, Yield | 11.8 MPa | 1710 psi | ASTM D638 |
| Elongation at Break | >= 200 % | >= 200 % | ASTM D638 |
| 1% Secant Modulus | 294.2 MPa | 42670 psi | ASTM D638 |
| Thermal Properties | Metric | English | Comments |
| Vicat Softening Point | 85.0 °C | 185 °F | resin; ASTM D1525 |
| Brittleness Temperature | <= -70.0 °C | <= -94.0 °F | ASTM D746 |
| Processing Properties | Metric | English | Comments |
| Melt Temperature | 170 - 220 °C | 338 - 428 °F | |
| Mold Temperature | 10.0 - 40.0 °C | 50.0 - 104 °F | |