- 熔體流動速率 [g/10min]: 20.0
- 密度 [g/cm3]: 0.92
- 拉伸強度 [MPa]: 11.7
- 彎曲模量 [MPa]: 0.210
- 脆化溫度 [℃]: -76.0
| Physical Properties | Metric | English | Comments | ||
|---|---|---|---|---|---|
| Density | 0.920 g/cc | 0.0332 lb/in3 | ASTM D1505 | ||
| Melt Flow | 20 g/10 min @Load 2.16 kg, Temperature 190 °C | 20 g/10 min @Load 4.76 lb, Temperature 374 °F | ASTM D1238 | ||
| Mechanical Properties | Metric | English | Comments | ||
| Hardness, Shore D | 51 | 51 | ASTM D-2240 | ||
| Tensile Strength, Yield | 11.7 MPa | 1700 psi | 2 in/min (50 mm/min); ASTM D638 | ||
| Elongation at Break | 400 % | 400 % | 2 in/min (50 mm/min); ASTM D638 | ||
| Modulus of Elasticity | 0.213 GPa | 30.9 ksi | ASTM D-638 | ||
| Flexural Modulus | 0.210 GPa | 30.5 ksi | Tangent Method 1; ASTM D-790 | ||
| Izod Impact, Notched | NB | NB | ASTM D256 | ||
| Thermal Properties | Metric | English | Comments | ||
| Vicat Softening Point | 101 °C | 214 °F | ASTM D1525 | ||
| Brittleness Temperature | <= -76.0 °C | <= -105 °F | ASTM D-746 | ||
| Descriptive Properties | |||||
| process | Injection Molding | ||||
| region | Europe/Turkey | ||||
| International | |||||
| Mexico | |||||
| US & Canada | |||||