- 熔體流動(dòng)速率 [g/10min]: 2.0
- 密度 [g/cm3]: 0.918
| Physical Properties | Metric | English | Comments | ||
|---|---|---|---|---|---|
| Density | 0.918 g/cc | 0.0332 lb/in3 | ASTM D792 | ||
| Melt Flow | 2.0 g/10 min @Load 2.16 kg, Temperature 190 °C | 2.0 g/10 min @Load 4.76 lb, Temperature 374 °F | ASTM D1238 | ||
| Mechanical Properties | Metric | English | Comments | ||
| Film Tensile Strength at Yield, MD | 10.0 MPa | 1450 psi | ASTM D882 | ||
| Film Tensile Strength at Yield, TD | 9.00 MPa | 1310 psi | ASTM D882 | ||
| Film Elongation at Break, MD | 690 % | 690 % | ASTM D882 | ||
| Film Elongation at Break, TD | 740 % | 740 % | ASTM D882 | ||
| Secant Modulus, MD | 0.180 GPa | 26.1 ksi | at 1%; ASTM D882 | ||
| Secant Modulus, TD | 0.200 GPa | 29.0 ksi | at 1%; ASTM D882 | ||
| Impact | 60 | 60 | J/mm; NOVA Chemicals Puncture test | ||
| Coefficient of Friction | >= 0.60 | >= 0.60 | ASTM D1894 | ||
| Elmendorf Tear Strength, MD | 3.50 g/micron | 88.9 g/mil | ASTM D1922 | ||
| Elmendorf Tear Strength, TD | 10.6 g/micron | 269 g/mil | ASTM D1922 | ||
| Dart Drop | 3.00 g/micron | 76.2 g/mil | F50, ASTM D1709/A | ||
| Film Tensile Strength at Break, MD | 30.0 MPa | 4350 psi | ASTM D882 | ||
| Film Tensile Strength at Break, TD | 25.0 MPa | 3630 psi | ASTM D882 | ||
| Optical Properties | Metric | English | Comments | ||
| Haze | 14 % | 14 % | ASTM D1003 | ||
| Gloss | 50 % | 50 % | at 45°; ASTM D2457 | ||
| Processing Properties | Metric | English | Comments | ||
| Melt Temperature | 195 - 205 °C | 383 - 401 °F | |||
| Descriptive Properties | |||||
| Blow Up Ratio | 2:1 to 3:1 | ||||