- 熔體流動速率 [g/10min]: 1.8
- 密度 [g/cm3]: 0.942
| Physical Properties | Metric | English | Comments |
|---|---|---|---|
| Density | 0.942 g/cc | 0.0340 lb/in3 | ASTM D792 |
| Melt Flow | 1.8 g/10 min @Load 2.16 kg, Temperature 190 °C | 1.8 g/10 min @Load 4.76 lb, Temperature 374 °F | ASTM D1238 |
| Mechanical Properties | Metric | English | Comments |
| Film Tensile Strength at Yield, MD | 17.0 MPa | 2470 psi | ASTM D882 |
| Film Tensile Strength at Yield, TD | 17.0 MPa | 2470 psi | ASTM D882 |
| Film Elongation at Break, MD | 600 % | 600 % | ASTM D882 |
| Film Elongation at Break, TD | 1000 % | 1000 % | ASTM D882 |
| Secant Modulus, MD | 0.385 GPa | 55.8 ksi | at 1%; ASTM D882 |
| Secant Modulus, TD | 0.450 GPa | 65.3 ksi | at 1%; ASTM D882 |
| Impact | 70 | 70 | J/mm; NOVA Chemicals Puncture test |
| Elmendorf Tear Strength, MD | 1.00 g/micron | 25.4 g/mil | ASTM D1922 |
| Elmendorf Tear Strength, TD | 12.0 g/micron | 305 g/mil | ASTM D1922 |
| Film Tensile Strength at Break, MD | 48.0 MPa | 6960 psi | ASTM D882 |
| Film Tensile Strength at Break, TD | 35.0 MPa | 5080 psi | ASTM D882 |
| Optical Properties | Metric | English | Comments |
| Haze | 4.0 % | 4.0 % | ASTM D1003 |
| Gloss | 87 % | 87 % | at 45°; ASTM D2457 |