- 熔體流動(dòng)速率 [g/10min]: 1.0
- 密度 [g/cm3]: 0.917
| Physical Properties | Metric | English | Comments |
|---|---|---|---|
| Density | 0.917 g/cc | 0.0331 lb/in3 | ASTM D792 |
| Thickness | 25.0 microns | 0.984 mil | |
| Melt Flow | 1.0 g/10 min @Load 2.16 kg, Temperature 190 °C | 1.0 g/10 min @Load 4.76 lb, Temperature 374 °F | ASTM D1238 |
| Mechanical Properties | Metric | English | Comments |
| Film Tensile Strength at Yield, MD | 9.03 MPa | 1310 psi | ASTM D882 |
| Film Tensile Strength at Yield, TD | 9.03 MPa | 1310 psi | ASTM D882 |
| Film Elongation at Yield, MD | 520 % | 520 % | ASTM D638 |
| Film Elongation at Yield, TD | 750 % | 750 % | ASTM D882 |
| Puncture Energy | 2.10 J | 1.55 ft-lb | Low Friction Puncture |
| Elmendorf Tear Strength MD | 280 g | 280 g | ASTM D1922 |
| Elmendorf Tear Strength TD | 445 g | 445 g | ASTM D1922 |
| Dart drop Test | >= 800 g | >= 1.76 lb | ASTM D1709/A |
| Film Tensile Strength at Break, MD | 49.0 MPa | 7110 psi | ASTM D882 |
| Film Tensile Strength at Break, TD | 43.0 MPa | 6240 psi | ASTM D882 |
| 1% Secant Modulus, MD | 135.0 MPa | 19580 psi | ASTM D882 |
| 1% Secant Modulus, TD | 155.0 MPa | 22480 psi | ASTM D882 |
| Heat Seal Strength Initiation Temperature | 100 °C | 212 °F | 2N |
| Optical Properties | Metric | English | Comments |
| Haze | 4.0 % | 4.0 % | ASTM D1003 |
| Gloss | 79 % | 79 % | at 45°; ASTM D2457 |
| Processing Properties | Metric | English | Comments |
| Melt Temperature | 185 - 200 °C | 365 - 392 °F | |