- 熔體流動速率 [g/10min]: 1.0
- 密度 [g/cm3]: 0.92
| Physical Properties | Metric | English | Comments |
|---|---|---|---|
| Density | 0.920 g/cc | 0.0332 lb/in3 | ASTM D792 |
| Thickness | 25.0 microns | 0.984 mil | |
| Melt Flow | 1.0 g/10 min @Load 2.16 kg, Temperature 190 °C | 1.0 g/10 min @Load 4.76 lb, Temperature 374 °F | ASTM D1238 |
| Mechanical Properties | Metric | English | Comments |
| Film Tensile Strength at Yield, MD | 10.0 MPa | 1450 psi | ASTM D882 |
| Film Tensile Strength at Yield, TD | 10.0 MPa | 1450 psi | ASTM D882 |
| Film Elongation at Yield, MD | 480 % | 480 % | ASTM D638 |
| Film Elongation at Yield, TD | 670 % | 670 % | ASTM D882 |
| Puncture Energy | 0.900 J | 0.664 ft-lb | Low Friction Puncture |
| Elmendorf Tear Strength MD | 420 g | 420 g | ASTM D1922 |
| Elmendorf Tear Strength TD | 605 g | 605 g | ASTM D1922 |
| Dart drop Test | 270 g | 0.595 lb | ASTM D1709/A |
| Film Tensile Strength at Break, MD | 48.0 MPa | 6960 psi | ASTM D882 |
| Film Tensile Strength at Break, TD | 32.0 MPa | 4640 psi | ASTM D882 |
| 1% Secant Modulus, MD | 174.95 MPa | 25375 psi | ASTM D882 |
| 1% Secant Modulus, TD | 194.95 MPa | 28275 psi | ASTM D882 |
| Optical Properties | Metric | English | Comments |
| Haze | 10 % | 10 % | ASTM D1003 |
| Gloss | 59 % | 59 % | at 45°; ASTM D2457 |
| Processing Properties | Metric | English | Comments |
| Melt Temperature | 210 - 230 °C | 410 - 446 °F | |