- 熔體流動速率 [g/10min]: 20.0
- 密度 [g/cm3]: 0.924
- 拉伸強度 [MPa]: 12.4
- 彎曲模量 [MPa]: 0.375
| Physical Properties | Metric | English | Comments |
|---|---|---|---|
| Bulk Density | 0.720 g/cc | 0.0260 lb/in3 | ASTM D 792 |
| Density | 0.924 g/cc | 0.0334 lb/in3 | ASTM D 792 |
| Melt Flow | 20 g/10 min @Load 2.16 kg, Temperature 190 °C | 20 g/10 min @Load 4.76 lb, Temperature 374 °F | ASTM D 1238 |
| Mechanical Properties | Metric | English | Comments |
| Hardness, Shore D | 56 | 56 | ASTM D 2240 |
| Tensile Strength at Break | 9.00 MPa | 1310 psi | 50 mm/min test speed; ASTM D 638 |
| Tensile Strength, Yield | 12.4 MPa | 1800 psi | 50 mm/min test speed; ASTM D 638 |
| Elongation at Break | 550 % | 550 % | 50 mm/min test speed; ASTM D 638 |
| Flexural Modulus | 0.375 GPa | 54.4 ksi | ASTM D 790 |
| Thermal Properties | Metric | English | Comments |
| Vicat Softening Point | 92.0 °C | 198 °F | ASTM D 1525 |
| Processing Properties | Metric | English | Comments |
| Melt Temperature | 170 - 215 °C | 338 - 419 °F | Recommended |