- 熔體流動速率 [g/10min]: 0.72
- 密度 [g/cm3]: 0.92
| Physical Properties | Metric | English | Comments | ||
|---|---|---|---|---|---|
| Density | 0.920 g/cc | 0.0332 lb/in3 | ASTM D792 | ||
| Thickness | 25.0 - 75.0 microns | 0.984 - 2.95 mil | |||
| Melt Flow | 0.72 g/10 min @Load 2.16 kg, Temperature 190 °C | 0.72 g/10 min @Load 4.76 lb, Temperature 374 °F | ASTM D1238 | ||
| Mechanical Properties | Metric | English | Comments | ||
| Film Tensile Strength at Yield, MD | 10.0 MPa | 1450 psi | ASTM D882 | ||
| Film Tensile Strength at Yield, TD | 11.0 MPa | 1600 psi | ASTM D882 | ||
| Film Elongation at Break, MD | 620 % | 620 % | ASTM D882 | ||
| Film Elongation at Break, TD | 920 % | 920 % | ASTM D882 | ||
| Secant Modulus, MD | 0.180 GPa | 26.1 ksi | at 1%; ASTM D882 | ||
| Secant Modulus, TD | 0.200 GPa | 29.0 ksi | at 1%; ASTM D882 | ||
| Coefficient of Friction | >= 1.0 | >= 1.0 | ASTM D1894 | ||
| Elmendorf Tear Strength, MD | 18.0 g/micron | 457 g/mil | ASTM D1922 | ||
| Elmendorf Tear Strength, TD | 26.0 g/micron | 660 g/mil | ASTM D1922 | ||
| Dart Drop | 8.00 g/micron | 203 g/mil | F50, ASTM D1709/A | ||
| Film Tensile Strength at Break, MD | 43.0 MPa | 6240 psi | ASTM D882 | ||
| Film Tensile Strength at Break, TD | 36.0 MPa | 5220 psi | ASTM D882 | ||
| Optical Properties | Metric | English | Comments | ||
| Haze | 11 % | 11 % | 1 mil; ASTM D1003 | ||
| Gloss | 51 % | 51 % | at 45°; 1 mil; ASTM D2457 | ||
| Processing Properties | Metric | English | Comments | ||
| Melt Temperature | 220 - 230 °C | 428 - 446 °F | |||
| Die Opening | 0.0900 - 0.220 cm | 0.0354 - 0.0866 in | |||
| Descriptive Properties | |||||
| Blow Up Ratio | 2:1 to 3:1 | ||||
Materials flagged as discontinued () are no longer part of the manufacturer’s standard product line according to our latest information. These materials may be available by special order, in distribution inventory, or reinstated as an active product. Data sheets from materials that are no longer available remain in MatWeb to assist users in finding replacement materials.
Users of our Advanced Search (registration required) may exclude discontinued materials from search results.