- 熔體流動速率 [g/10min]: 8.0
- 密度 [g/cm3]: 0.934
- 拉伸強度 [MPa]: 16.0
- 彎曲模量 [MPa]: 0.610
- 脆化溫度 [℃]: -70.0
| Physical Properties | Metric | English | Comments | ||
|---|---|---|---|---|---|
| Density | 0.934 g/cc | 0.0337 lb/in3 | ASTM D792 | ||
| Melt Flow | 8.0 - 10 g/10 min | 8.0 - 10 g/10 min | ASTM D1238 | ||
| Mechanical Properties | Metric | English | Comments | ||
| Tensile Strength, Yield | 16.0 MPa | 2320 psi | 50mm/min; ASTM D638-64T | ||
| Elongation at Break | 650 % | 650 % | ASTM D638-64T | ||
| Flexural Modulus | 0.610 GPa | 88.5 ksi | ASTM D760-66 | ||
| Thermal Properties | Metric | English | Comments | ||
| Vicat Softening Point | 111 °C | 232 °F | ASTM D1525 | ||
| Brittleness Temperature | <= -70.0 °C | <= -94.0 °F | ASTM D746 | ||
| Flammability, UL94 | V-2 | V-2 | |||
| Oxygen Index | 26 % | 26 % | Critical | ||
| Descriptive Properties | |||||
| British Standard 2782:508A | Zero Burn Rate | ||||
| British Standard 476 Part 7 | Class 2 | ||||
| Civil Aviation Authority Spec No 8 Vertical Test | Pass | ||||
| Stores Materials Container Fire Test | Pass | British Aerospace Std | |||