- 熔體流動(dòng)速率 [g/10min]: 0.95
- 密度 [g/cm3]: 0.912
- 透光率 [%]: 90.0
| Physical Properties | Metric | English | Comments |
|---|---|---|---|
| Density | 0.912 g/cc | 0.0329 lb/in3 | ASTM D792 |
| Thickness | 25.4 microns | 1.00 mil | |
| Melt Flow | 0.95 g/10 min @Load 2.16 kg, Temperature 230 °C | 0.95 g/10 min @Load 4.76 lb, Temperature 446 °F | ASTM D1238 |
| Mechanical Properties | Metric | English | Comments |
| Film Tensile Strength at Yield, MD | 12.4 MPa | 1800 psi | ASTM D882 |
| Film Elongation at Break, MD | 600 % | 600 % | ASTM D882 |
| Film Elongation at Break, TD | 800 % | 800 % | ASTM D882 |
| Secant Modulus, MD | 0.179 GPa | 26.0 ksi | ASTM D882 |
| Secant Modulus, TD | 0.193 GPa | 28.0 ksi | ASTM D882 |
| Elmendorf Tear Strength MD | 100 g | 100 g | ASTM D1922A |
| Elmendorf Tear Strength TD | 460 g | 460 g | ASTM D1922A |
| Elmendorf Tear Strength, MD | 3.94 g/micron | 100 g/mil | ASTM D1922A |
| Elmendorf Tear Strength, TD | 18.1 g/micron | 460 g/mil | ASTM D1922A |
| Dart Drop | 3.94 g/micron | 100 g/mil | ASTM D1709 |
| Dart drop Test | 100 g | 0.221 lb | ASTM D1709A |
| Film Tensile Strength at Break, MD | 37.9 MPa | 5500 psi | ASTM D882 |
| Film Tensile Strength at Break, TD | 31.0 MPa | 4500 psi | ASTM D882 |
| Optical Properties | Metric | English | Comments |
| Gloss | 70 - 80 % | 70 - 80 % | at 45°; ASTM D523 |
| Transmission, Visible | 90.0 % | 90.0 % | clear; thickness not quantified |