- 熔體流動速率 [g/10min]: 3.8
- 密度 [g/cm3]: 0.938
- 拉伸強度 [MPa]: 19.0
| Physical Properties | Metric | English | Comments |
|---|---|---|---|
| Density | 0.938 g/cc | 0.0339 lb/in3 | ASTM D792 |
| Melt Flow | 3.8 g/10 min @Load 2.16 kg, Temperature 190 °C | 3.8 g/10 min @Load 4.76 lb, Temperature 374 °F | ASTM D1238 |
| 10.4 g/10 min @Load 5.00 kg, Temperature 190 °C | 10.4 g/10 min @Load 11.0 lb, Temperature 374 °F | ASTM D1238 | |
| Mechanical Properties | Metric | English | Comments |
| Tensile Strength, Yield | 19.0 MPa | 2760 psi | 50mm/min; ASTM D638-64T |
| Elongation at Break | 239 % | 239 % | ASTM D638-64T |
| Modulus of Elasticity | 0.685 GPa | 99.4 ksi | ASTM D638 |
| Charpy Impact, Notched | 0.884 J/cm2 | 4.21 ft-lb/in2 | Room Temperature |
| Impact | 16.4 @Temperature -20.0 °C | 16.4 @Temperature -4.00 °F | J/mm, Falling weight impact; ARM |
| Thermal Properties | Metric | English | Comments |
| Vicat Softening Point | 117 °C | 243 °F | ASTM D1525 |