- 熔體流動速率 [g/10min]: 4.0
- 密度 [g/cm3]: 0.945
- 拉伸強度 [MPa]: 22.0
- 彎曲模量 [MPa]: 1.05
- 脆化溫度 [℃]: -70.0
| Physical Properties | Metric | English | Comments |
|---|---|---|---|
| Density | 0.945 g/cc | 0.0341 lb/in3 | ASTM D792 |
| Melt Flow | 4.0 - 6.0 g/10 min | 4.0 - 6.0 g/10 min | ASTM D1238 |
| Mechanical Properties | Metric | English | Comments |
| Tensile Strength, Yield | 22.0 MPa | 3190 psi | 50mm/min; ASTM D638-64T |
| Elongation at Break | 500 % | 500 % | ASTM D638-64T |
| Flexural Modulus | 1.05 GPa | 152 ksi | ASTM D760-66 |
| Thermal Properties | Metric | English | Comments |
| Vicat Softening Point | 114 °C | 237 °F | ASTM D1525 |
| Brittleness Temperature | <= -70.0 °C | <= -94.0 °F | ASTM D746 |