- 熔體流動速率 [g/10min]: 0.95
- 密度 [g/cm3]: 0.916
| Physical Properties | Metric | English | Comments |
|---|---|---|---|
| Density | 0.916 g/cc | 0.0331 lb/in3 | ASTM D792 |
| Thickness | 25.4 microns | 1.00 mil | |
| Melt Flow | 0.95 g/10 min @Load 2.16 kg, Temperature 230 °C | 0.95 g/10 min @Load 4.76 lb, Temperature 446 °F | ASTM D1238 |
| Mechanical Properties | Metric | English | Comments |
| Film Tensile Strength at Yield, MD | 11.0 MPa | 1600 psi | ASTM D882 |
| Film Tensile Strength at Yield, TD | 11.0 MPa | 1600 psi | ASTM D882 |
| Film Elongation at Break, MD | 800 % | 800 % | ASTM D882 |
| Film Elongation at Break, TD | 1000 % | 1000 % | ASTM D882 |
| Secant Modulus, MD | 0.179 GPa | 26.0 ksi | ASTM D882 |
| Secant Modulus, TD | 0.193 GPa | 28.0 ksi | ASTM D882 |
| Elmendorf Tear Strength MD | 150 g | 150 g | ASTM D1922A |
| Elmendorf Tear Strength TD | 450 g | 450 g | ASTM D1922A |
| Elmendorf Tear Strength, MD | 5.91 g/micron | 150 g/mil | ASTM D1922A |
| Elmendorf Tear Strength, TD | 17.7 g/micron | 450 g/mil | ASTM D1922A |
| Dart Drop | 4.13 g/micron | 105 g/mil | ASTM D1709 |
| Dart drop Test | 105 g | 0.232 lb | ASTM D1709A |
| Film Tensile Strength at Break, MD | 42.1 MPa | 6110 psi | ASTM D882 |
| Film Tensile Strength at Break, TD | 30.3 MPa | 4390 psi | ASTM D882 |