- 熔體流動速率 [g/10min]: 3.0
- 密度 [g/cm3]: 0.934
- 拉伸強(qiáng)度 [MPa]: 16.0
- 彎曲模量 [MPa]: 0.610
- 脆化溫度 [℃]: -70.0
| Physical Properties | Metric | English | Comments |
|---|---|---|---|
| Density | 0.934 g/cc | 0.0337 lb/in3 | ASTM D792 |
| Melt Flow | 3.0 - 4.0 g/10 min | 3.0 - 4.0 g/10 min | ASTM D1238 |
| Mechanical Properties | Metric | English | Comments |
| Tensile Strength, Yield | 16.0 MPa | 2320 psi | 50mm/min; ASTM D638-64T |
| Elongation at Break | 650 % | 650 % | ASTM D638-64T |
| Flexural Modulus | 0.610 GPa | 88.5 ksi | ASTM D760-66 |
| Thermal Properties | Metric | English | Comments |
| Vicat Softening Point | 111 °C | 232 °F | ASTM D1525 |
| Brittleness Temperature | <= -70.0 °C | <= -94.0 °F | ASTM D746 |