- 熔體流動速率 [g/10min]: 2.0
- 密度 [g/cm3]: 0.916
| Physical Properties | Metric | English | Comments |
|---|---|---|---|
| Density | 0.916 g/cc | 0.0331 lb/in3 | ASTM D792 |
| Thickness | 25.4 microns | 1.00 mil | |
| Melt Flow | 2.0 g/10 min @Load 2.16 kg, Temperature 230 °C | 2.0 g/10 min @Load 4.76 lb, Temperature 446 °F | ASTM D1238 |
| Mechanical Properties | Metric | English | Comments |
| Film Tensile Strength at Yield, MD | 11.0 MPa | 1600 psi | ASTM D882 |
| Film Tensile Strength at Yield, TD | 11.0 MPa | 1600 psi | ASTM D882 |
| Film Elongation at Break, MD | 800 % | 800 % | ASTM D882 |
| Film Elongation at Break, TD | 900 % | 900 % | ASTM D882 |
| Secant Modulus, MD | 0.152 GPa | 22.0 ksi | ASTM D882 |
| Secant Modulus, TD | 0.172 GPa | 24.9 ksi | ASTM D882 |
| Elmendorf Tear Strength MD | 40 g | 40 g | ASTM D1922A |
| Elmendorf Tear Strength TD | 350 g | 350 g | ASTM D1922A |
| Elmendorf Tear Strength, MD | 1.57 g/micron | 40.0 g/mil | ASTM D1922A |
| Elmendorf Tear Strength, TD | 13.8 g/micron | 350 g/mil | ASTM D1922A |
| Dart Drop | 3.54 g/micron | 90.0 g/mil | ASTM D1709 |
| Dart drop Test | 90.0 g | 0.198 lb | ASTM D1709A |
| Film Tensile Strength at Break, MD | 37.9 MPa | 5500 psi | ASTM D882 |
| Film Tensile Strength at Break, TD | 29.0 MPa | 4210 psi | ASTM D882 |