- 熔體流動速率 [g/10min]: 4.0
- 密度 [g/cm3]: 0.924
- 拉伸強度 [MPa]: 10.0
- 彎曲模量 [MPa]: 0.245
- 脆化溫度 [℃]: -70.0
| Physical Properties | Metric | English | Comments | ||
|---|---|---|---|---|---|
| Density | 0.924 g/cc | 0.0334 lb/in3 | ASTM D792 | ||
| Melt Flow | 4.0 - 6.0 g/10 min | 4.0 - 6.0 g/10 min | ASTM D1238 | ||
| Mechanical Properties | Metric | English | Comments | ||
| Tensile Strength, Yield | 10.0 MPa | 1450 psi | 50mm/min; ASTM D638-64T | ||
| Elongation at Break | 840 % | 840 % | ASTM D638-64T | ||
| Flexural Modulus | 0.245 GPa | 35.5 ksi | ASTM D760-66 | ||
| Thermal Properties | Metric | English | Comments | ||
| Vicat Softening Point | 91.0 °C | 196 °F | ASTM D1525 | ||
| Brittleness Temperature | <= -70.0 °C | <= -94.0 °F | ASTM D746 | ||
| Flammability, UL94 | V-2 | V-2 | |||
| Oxygen Index | 26 % | 26 % | Critical | ||
| Descriptive Properties | |||||
| British Standard 2782:508A | Zero Burn Rate | ||||
| British Standard 476 Part 7 | Class 2 | ||||
| Civil Aviation Authority Spec No 8 Vertical Test | Pass | ||||
| Stores Materials Container Fire Test | Pass | ||||