- 熔體流動速率 [g/10min]: 0.9
- 密度 [g/cm3]: 0.917
| Physical Properties | Metric | English | Comments |
|---|---|---|---|
| Density | 0.917 g/cc | 0.0331 lb/in3 | ASTM D1505 |
| Thickness | 25.0 microns | 0.984 mil | |
| Melt Flow | 0.90 g/10 min @Load 2.16 kg, Temperature 190 °C | 0.90 g/10 min @Load 4.76 lb, Temperature 374 °F | Condition E; ASTM D1238 |
| Antiblock Level | 7000 ppm | 7000 ppm | |
| Mechanical Properties | Metric | English | Comments |
| Film Tensile Strength at Yield, MD | 11.41 MPa | 1655 psi | ASTM D882 |
| Film Tensile Strength at Yield, TD | 11.27 MPa | 1635 psi | ASTM D882 |
| Film Elongation at Break, MD | 700 % | 700 % | ASTM D882 |
| Film Elongation at Break, TD | 870 % | 870 % | ASTM D882 |
| Elmendorf Tear Strength MD | 375 g | 375 g | ASTM D1922 |
| Elmendorf Tear Strength TD | 705 g | 705 g | ASTM D1922 |
| Dart drop Test | 405 g | 0.893 lb | ASTM D1709 |
| Film Tensile Strength at Break, MD | 39.2 MPa | 5680 psi | ASTM D882 |
| Film Tensile Strength at Break, TD | 29.6 MPa | 4290 psi | ASTM D882 |
| Processing Properties | Metric | English | Comments |
| Blow-up Ratio (BUR) | 2.5 | 2.5 | |