- 熔體流動速率 [g/10min]: 0.95
- 密度 [g/cm3]: 0.919
| Physical Properties | Metric | English | Comments | ||
|---|---|---|---|---|---|
| Density | 0.919 g/cc | 0.0332 lb/in3 | ASTM D1505 | ||
| Thickness | 25.0 microns | 0.984 mil | |||
| Melt Flow | 0.95 g/10 min @Load 2.16 kg, Temperature 190 °C | 0.95 g/10 min @Load 4.76 lb, Temperature 374 °F | Condition E; ASTM D1238 | ||
| Mechanical Properties | Metric | English | Comments | ||
| Film Elongation at Break, MD | 520 % | 520 % | ASTM D882 | ||
| Film Elongation at Break, TD | 780 % | 780 % | ASTM D882 | ||
| Elmendorf Tear Strength, MD | 15.7 g/micron | 400 g/mil | ASTM D1922 | ||
| Elmendorf Tear Strength, TD | 24.8 g/micron | 630 g/mil | ASTM D1922 | ||
| Dart Drop | 6.30 g/micron | 160 g/mil | ASTM D1709 | ||
| Film Tensile Strength at Break, MD | 32.8 MPa | 4750 psi | ASTM D882 | ||
| Film Tensile Strength at Break, TD | 24.0 MPa | 3490 psi | ASTM D882 | ||
| Thermal Properties | Metric | English | Comments | ||
| Antiblock | 7000 | 7000 | [ppm] | ||
| Optical Properties | Metric | English | Comments | ||
| Haze | 21 % | 21 % | ASTM D1003 | ||
| Gloss | 33 % | 33 % | 45°; ASTM D2457 | ||
| Descriptive Properties | |||||
| Blow Up Ratio | 4 to 1 | ||||