- 熔體流動速率 [g/10min]: 3.2
- 密度 [g/cm3]: 0.918
| Physical Properties | Metric | English | Comments | ||
|---|---|---|---|---|---|
| Density | 0.918 g/cc | 0.0332 lb/in3 | ASTM D1505 | ||
| Thickness | 25.0 microns | 0.984 mil | |||
| Melt Flow | 3.2 g/10 min @Load 2.16 kg, Temperature 190 °C | 3.2 g/10 min @Load 4.76 lb, Temperature 374 °F | Condition E; ASTM D1238 | ||
| Mechanical Properties | Metric | English | Comments | ||
| Film Elongation at Break, MD | 550 % | 550 % | ASTM D882 | ||
| Film Elongation at Break, TD | 850 % | 850 % | ASTM D882 | ||
| Elmendorf Tear Strength, MD | 10.8 g/micron | 275 g/mil | ASTM D1922 | ||
| Elmendorf Tear Strength, TD | 22.6 g/micron | 575 g/mil | ASTM D1922 | ||
| Dart Drop | 3.54 g/micron | 90.0 g/mil | ASTM D1709 | ||
| Film Tensile Strength at Break, MD | 44.82 MPa | 6500 psi | ASTM D882 | ||
| Film Tensile Strength at Break, TD | 33.09 MPa | 4800 psi | ASTM D882 | ||
| Optical Properties | Metric | English | Comments | ||
| Haze | 1.4 % | 1.4 % | ASTM D1003 | ||
| Gloss | 98 % | 98 % | 45°; ASTM D2457 | ||
| Descriptive Properties | |||||
| Blow Up Ratio | 4 to 1 | ||||