- 熔體流動速率 [g/10min]: 0.8
- 密度 [g/cm3]: 0.926
| Physical Properties | Metric | English | Comments |
|---|---|---|---|
| Density | 0.926 g/cc | 0.0335 lb/in3 | ASTM D1505 |
| Thickness | 25.0 microns | 0.984 mil | |
| Melt Flow | 0.80 g/10 min @Load 2.16 kg, Temperature 190 °C | 0.80 g/10 min @Load 4.76 lb, Temperature 374 °F | Condition E; ASTM D1238 |
| Antiblock Level | 500 ppm | 500 ppm | |
| Mechanical Properties | Metric | English | Comments |
| Film Elongation at Break, MD | 490 % | 490 % | ASTM D882 |
| Film Elongation at Break, TD | 700 % | 700 % | ASTM D882 |
| Elmendorf Tear Strength MD | 250 g | 250 g | ASTM D1922 |
| Elmendorf Tear Strength TD | 650 g | 650 g | ASTM D1922 |
| Dart drop Test | 100 g | 0.221 lb | ASTM D1709 |
| Film Tensile Strength at Break, MD | 32.4 MPa | 4700 psi | ASTM D882 |
| Film Tensile Strength at Break, TD | 22.58 MPa | 3275 psi | ASTM D882 |
| Optical Properties | Metric | English | Comments |
| Haze | 28 % | 28 % | ASTM D1003 |
| Gloss | 25 % | 25 % | 45°C; ASTM D523 |
| Processing Properties | Metric | English | Comments |
| Blow-up Ratio (BUR) | 2.5 | 2.5 | |