- 熔體流動速率 [g/10min]: 4.0
- 密度 [g/cm3]: 0.938
- 拉伸強(qiáng)度 [MPa]: 22.8
- 彎曲模量 [MPa]: 0.758
- 熱變形溫度 [℃]: 56.0
| Physical Properties | Metric | English | Comments |
|---|---|---|---|
| Density | 0.938 g/cc | 0.0339 lb/in3 | ASTM D1505 |
| Environmental Stress Crack Resistance | >= 1000 hour | >= 1000 hour | Condition A (100% Igepal), F50; ASTM D1693 |
| Melt Flow | 4.0 g/10 min | 4.0 g/10 min | ASTM D1238 |
| Mechanical Properties | Metric | English | Comments |
| Tensile Strength, Yield | 22.8 MPa | 3300 psi | 2" (50mm) per min.; ASTM D638 |
| Elongation at Yield | 11.3 % | 11.3 % | 2" (50mm) per min.; ASTM D638 |
| Flexural Modulus | 0.758 GPa | 110 ksi | 1.3mm per min; ASTM D790 |
| Thermal Properties | Metric | English | Comments |
| Deflection Temperature at 0.46 MPa (66 psi) | 56.0 °C | 133 °F | ASTM D648 |