- 熔體流動速率 [g/10min]: 0.95
- 密度 [g/cm3]: 0.919
| Physical Properties | Metric | English | Comments | ||
|---|---|---|---|---|---|
| Density | 0.919 g/cc | 0.0332 lb/in3 | ASTM D1505 | ||
| Thickness | 25.0 microns | 0.984 mil | |||
| Melt Flow | 0.95 g/10 min @Load 2.16 kg, Temperature 190 °C | 0.95 g/10 min @Load 4.76 lb, Temperature 374 °F | Condition E; ASTM D1238 | ||
| Mechanical Properties | Metric | English | Comments | ||
| Film Elongation at Break, MD | 700 % | 700 % | ASTM D882 | ||
| Film Elongation at Break, TD | 815 % | 815 % | ASTM D882 | ||
| Elmendorf Tear Strength, MD | 6.30 g/micron | 160 g/mil | ASTM D1922 | ||
| Elmendorf Tear Strength, TD | 15.7 g/micron | 400 g/mil | ASTM D1922 | ||
| Dart Drop | 5.31 g/micron | 135 g/mil | ASTM D1709 | ||
| Film Tensile Strength at Break, MD | 35.2 MPa | 5100 psi | ASTM D882 | ||
| Film Tensile Strength at Break, TD | 22.2 MPa | 3230 psi | ASTM D882 | ||
| Optical Properties | Metric | English | Comments | ||
| Haze | 27 % | 27 % | ASTM D1003 | ||
| Gloss | 36 % | 36 % | 45°; ASTM D523 | ||
| Descriptive Properties | |||||
| Blow Up Ratio | 4 to 1 | ||||