- 熔體流動速率 [g/10min]: 1.3
- 密度 [g/cm3]: 0.921
| Physical Properties | Metric | English | Comments |
|---|---|---|---|
| Density | 0.921 g/cc | 0.0333 lb/in3 | Exxon Method |
| Thickness | 30.5 microns | 1.20 mil | |
| Melt Flow | 1.3 g/10 min | 1.3 g/10 min | Exxon Method |
| Mechanical Properties | Metric | English | Comments |
| Film Tensile Strength at Yield, MD | 10.6 MPa | 1540 psi | ASTM D882 |
| Film Tensile Strength at Yield, TD | 11.9 MPa | 1730 psi | ASTM D882 |
| Film Elongation at Break, MD | 600 % | 600 % | ASTM D882 |
| Film Elongation at Break, TD | 730 % | 730 % | ASTM D882 |
| Secant Modulus, MD | 0.254 GPa | 36.8 ksi | ASTM D882 |
| Secant Modulus, TD | 0.261 GPa | 37.9 ksi | ASTM D882 |
| Elmendorf Tear Strength MD | 290 g | 290 g | ASTM D1922 |
| Elmendorf Tear Strength TD | 650 g | 650 g | ASTM D1922 |
| Elmendorf Tear Strength, MD | 9.53 g/micron | 242 g/mil | ASTM D1922 |
| Elmendorf Tear Strength, TD | 21.3 g/micron | 542 g/mil | ASTM D1922 |
| Dart Drop | 5.24 g/micron | 133 g/mil | F50; ASTM D1709 |
| Dart drop Test | 160 g | 0.353 lb | F50; ASTM D-1709 |
| Film Tensile Strength at Break, MD | 51.6 MPa | 7480 psi | ASTM D882 |
| Film Tensile Strength at Break, TD | 42.2 MPa | 6120 psi | ASTM D882 |
| Thermal Properties | Metric | English | Comments |
| Melting Point | 126 °C | 259 °F | Exxon Method |
| Optical Properties | Metric | English | Comments |
| Haze | 25 % | 25 % | ASTM D1003 |
| Gloss | 27 % | 27 % | 45°, ASTM D-2457 |