- 熔體流動速率 [g/10min]: 50.0
- 密度 [g/cm3]: 0.926
- 拉伸強度 [MPa]: 14.5
- 熱變形溫度 [℃]: 50.0
- 脆化溫度 [℃]: -76.0
| Physical Properties | Metric | English | Comments |
|---|---|---|---|
| Density | 0.926 g/cc | 0.0335 lb/in3 | ASTM D1505 |
| Melt Flow | 50 g/10 min | 50 g/10 min | ASTM D1238 |
| Spiral Flow | 49.0 cm | 19.3 in | Equistar test |
| Mechanical Properties | Metric | English | Comments |
| Hardness, Shore D | 52 | 52 | ASTM D2240 |
| Tensile Strength at Break | 10.3 MPa | 1500 psi | ASTM D638 |
| Tensile Strength, Yield | 14.5 MPa | 2100 psi | 20"/min; ASTM D638 |
| Elongation at Yield | 8.2 % | 8.2 % | 20"/min; ASTM D638 |
| 1% Secant Modulus | 441 MPa | 64000 psi | 0.5"/min; ASTM D790 |
| 2% Secant Modulus | 0.414 GPa | 60.0 ksi | 0.5"/min; ASTM D790 |
| Thermal Properties | Metric | English | Comments |
| Deflection Temperature at 0.46 MPa (66 psi) | 50.0 °C | 122 °F | ASTM D648 |
| Vicat Softening Point | 96.0 °C | 205 °F | ASTM D1525 |
| Brittleness Temperature | <= -76.0 °C | <= -105 °F | F50; ASTM D746 |
| Processing Properties | Metric | English | Comments |
| Rear Barrel Temperature | 177 °C | 350 °F | |
| Middle Barrel Temperature | 191 °C | 375 °F | |
| Front Barrel Temperature | 204 °C | 400 °F | |
| Nozzle Temperature | 204 °C | 400 °F | |