- 熔體流動(dòng)速率 [g/10min]: 21.0
- 密度 [g/cm3]: 0.924
- 拉伸強(qiáng)度 [MPa]: 13.8
- 熱變形溫度 [℃]: 47.0
- 脆化溫度 [℃]: -76.0
| Physical Properties | Metric | English | Comments |
|---|---|---|---|
| Density | 0.924 g/cc | 0.0334 lb/in3 | ASTM D1505 |
| Melt Flow | 21 g/10 min | 21 g/10 min | ASTM D1238 |
| Spiral Flow | 32.8 cm | 12.9 in | Equistar test |
| Mechanical Properties | Metric | English | Comments |
| Hardness, Shore D | 53 | 53 | ASTM D2240 |
| Tensile Strength at Break | 8.27 MPa | 1200 psi | ASTM D638 |
| Tensile Strength, Yield | 13.8 MPa | 2000 psi | 20"/min; ASTM D638 |
| Elongation at Yield | 12 % | 12 % | 20"/min; ASTM D638 |
| 1% Secant Modulus | 379 MPa | 55000 psi | 0.5"/min; ASTM D790 |
| 2% Secant Modulus | 0.317 GPa | 46.0 ksi | 0.5"/min; ASTM D790 |
| Thermal Properties | Metric | English | Comments |
| Deflection Temperature at 0.46 MPa (66 psi) | 47.0 °C | 117 °F | ASTM D648 |
| Vicat Softening Point | 96.0 °C | 205 °F | ASTM D1525 |
| Brittleness Temperature | <= -76.0 °C | <= -105 °F | F50; ASTM D746 |
| Processing Properties | Metric | English | Comments |
| Rear Barrel Temperature | 177 °C | 350 °F | |
| Middle Barrel Temperature | 191 °C | 375 °F | |
| Front Barrel Temperature | 204 °C | 400 °F | |
| Nozzle Temperature | 204 °C | 400 °F | |