- 熔體流動速率 [g/10min]: 4.5
- 密度 [g/cm3]: 0.927
| Physical Properties | Metric | English | Comments |
|---|---|---|---|
| Density | 0.927 g/cc | 0.0335 lb/in3 | ASTM D1505 |
| Water Vapor Transmission | 4.30 g/m2/day | 0.277 g/100 in2/day | ASTM F372 |
| Thickness | 50.8 microns | 2.00 mil | |
| Melt Flow | 4.5 g/10 min | 4.5 g/10 min | ASTM D1238 |
| Mechanical Properties | Metric | English | Comments |
| Film Tensile Strength at Yield, MD | 11.8 MPa | 1710 psi | ASTM D882 |
| Film Tensile Strength at Yield, TD | 13.8 MPa | 2000 psi | ASTM D882 |
| Film Elongation at Break, MD | 780 % | 780 % | ASTM D882 |
| Film Elongation at Break, TD | 840 % | 840 % | ASTM D882 |
| Film Elongation at Yield, MD | 12 % | 12 % | ASTM D882 |
| Film Elongation at Yield, TD | 9.0 % | 9.0 % | ASTM D882 |
| Elmendorf Tear Strength MD | 69 g | 69 g | ASTM D1922 |
| Elmendorf Tear Strength TD | 241 g | 241 g | ASTM D1922 |
| Film Tensile Strength at Break, MD | 22.9 MPa | 3320 psi | ASTM D882 |
| Film Tensile Strength at Break, TD | 2.10 MPa | 305 psi | ASTM D882 |
| Thermal Properties | Metric | English | Comments |
| Vicat Softening Point | 103 °C | 217 °F | ASTM D1525 |
| Processing Properties | Metric | English | Comments |
| Melt Temperature | >= 210 °C | >= 410 °F | |
| Blow-up Ratio (BUR) | 2.0 | 2.0 | |