- 熔體流動速率 [g/10min]: 2.3
- 密度 [g/cm3]: 0.917
- 拉伸強度 [MPa]: 10.3
- 彎曲強度 [MPa]: 13.1
| Physical Properties | Metric | English | Comments |
|---|---|---|---|
| Density | 0.917 g/cc | 0.0331 lb/in3 | |
| Thickness | 25.0 microns | 0.984 mil | |
| Melt Flow | 2.3 g/10 min @Load 2.16 kg | 2.3 g/10 min @Load 4.76 lb | Melt flow ratio I10/I2 is 7.6. |
| Mechanical Properties | Metric | English | Comments |
| Tensile Strength, Ultimate | 13.1 MPa | 1900 psi | Molded property |
| Film Tensile Strength at Yield, MD | 7.60 MPa | 1100 psi | |
| Film Tensile Strength at Yield, TD | 7.60 MPa | 1100 psi | |
| Tensile Strength, Yield | 10.3 MPa | 1490 psi | Molded property |
| Film Elongation at Break, MD | 510 % | 510 % | |
| Film Elongation at Break, TD | 760 % | 760 % | |
| Elongation at Break | 900 % | 900 % | Molded value |
| Elmendorf Tear Strength MD | 325 g | 325 g | |
| Elmendorf Tear Strength TD | 520 g | 520 g | |
| Elmendorf Tear Strength, MD | 13.0 g/micron | 330 g/mil | |
| Elmendorf Tear Strength, TD | 20.8 g/micron | 528 g/mil | |
| Dart Drop | 12.8 g/micron | 325 g/mil | |
| Film Tensile Strength at Break, MD | 62.7 MPa | 9090 psi | |
| Film Tensile Strength at Break, TD | 39.3 MPa | 5700 psi | |
| Thermal Properties | Metric | English | Comments |
| Vicat Softening Point | 99.0 °C | 210 °F | |
| Optical Properties | Metric | English | Comments |
| Haze | 0.90 % | 0.90 % | |
| Gloss | 95 % | 95 % | 45° |
| Processing Properties | Metric | English | Comments |
| Processing Temperature | 274 °C | 525 °F | Film extrusion temperature |