- 熔體流動速率 [g/10min]: 1.0
- 密度 [g/cm3]: 0.922
- 拉伸強度 [MPa]: 12.4
- 彎曲強度 [MPa]: 26.2
| Physical Properties | Metric | English | Comments |
|---|---|---|---|
| Density | 0.922 g/cc | 0.0333 lb/in3 | |
| Thickness | 25.0 microns | 0.984 mil | |
| Melt Flow | 1.0 g/10 min @Load 2.16 kg | 1.0 g/10 min @Load 4.76 lb | Melt flow ratio I10/I2 is 8. |
| Mechanical Properties | Metric | English | Comments |
| Tensile Strength, Ultimate | 26.2 MPa | 3800 psi | Molded property |
| Film Tensile Strength at Yield, MD | 11.0 MPa | 1600 psi | |
| Film Tensile Strength at Yield, TD | 12.1 MPa | 1750 psi | |
| Tensile Strength, Yield | 12.4 MPa | 1800 psi | Molded property |
| Film Elongation at Break, MD | 520 % | 520 % | |
| Film Elongation at Break, TD | 670 % | 670 % | |
| Elongation at Break | 1000 % | 1000 % | Molded value |
| Elmendorf Tear Strength MD | 260 g | 260 g | |
| Elmendorf Tear Strength TD | 640 g | 640 g | |
| Elmendorf Tear Strength, MD | 10.4 g/micron | 264 g/mil | |
| Elmendorf Tear Strength, TD | 25.6 g/micron | 650 g/mil | |
| Dart Drop | 8.40 g/micron | 213 g/mil | |
| Film Tensile Strength at Break, MD | 51.4 MPa | 7450 psi | |
| Film Tensile Strength at Break, TD | 37.2 MPa | 5400 psi | |
| Thermal Properties | Metric | English | Comments |
| Vicat Softening Point | 106 °C | 223 °F | |
| Optical Properties | Metric | English | Comments |
| Haze | 10 % | 10 % | |
| Gloss | 55 % | 55 % | 45° |
| Processing Properties | Metric | English | Comments |
| Processing Temperature | 226 °C | 439 °F | Film extrusion temperature |