- 熔體流動速率 [g/10min]: 3.3
- 密度 [g/cm3]: 0.916
- 拉伸強度 [MPa]: 9.7
- 彎曲強度 [MPa]: 20.0
| Physical Properties | Metric | English | Comments |
|---|---|---|---|
| Density | 0.916 g/cc | 0.0331 lb/in3 | |
| Melt Flow | 3.3 g/10 min @Load 2.16 kg | 3.3 g/10 min @Load 4.76 lb | Melt flow ratio I10/I2 is 7.6. |
| Mechanical Properties | Metric | English | Comments |
| Tensile Strength, Ultimate | 20.0 MPa | 2900 psi | Molded property |
| Film Tensile Strength at Yield, MD | 7.60 MPa | 1100 psi | |
| Film Tensile Strength at Yield, TD | 6.90 MPa | 1000 psi | |
| Tensile Strength, Yield | 9.70 MPa | 1410 psi | Molded property |
| Elongation at Break | 900 % | 900 % | |
| Film Tensile Strength at Break, MD | 54.5 MPa | 7900 psi | |
| Thermal Properties | Metric | English | Comments |
| Vicat Softening Point | 94.0 °C | 201 °F | |
| Processing Properties | Metric | English | Comments |
| Processing Temperature | 209 °C | 408 °F | Film extrusion temperature |