- 熔體流動速率 [g/10min]: 0.5
- 密度 [g/cm3]: 0.917
| Physical Properties | Metric | English | Comments |
|---|---|---|---|
| Density | 0.917 g/cc | 0.0331 lb/in3 | Base Resin; ASTM D4833-89 |
| Thickness | 25.4 microns | 1.00 mil | |
| Melt Flow | 0.50 g/10 min | 0.50 g/10 min | ASTM D1238E |
| Slip Level | 0.000 ppm | 0.000 ppm | |
| Mechanical Properties | Metric | English | Comments |
| Film Elongation at Break, MD | 550 % | 550 % | ASTM D882 |
| Film Elongation at Break, TD | 690 % | 690 % | ASTM D882 |
| Coefficient of Friction | 1.0 | 1.0 | ASTM D1894 |
| Elmendorf Tear Strength, MD | 20.9 g/micron | 530 g/mil | Notched; ASTM D1922 |
| Elmendorf Tear Strength, TD | 31.1 g/micron | 790 g/mil | ASTM D1992 |
| Film Tensile Strength at Break, MD | 51.5 MPa | 7470 psi | ASTM D882 |
| Film Tensile Strength at Break, TD | 40.7 MPa | 5900 psi | ASTM D882 |
| 1% Secant Modulus, MD | 179 MPa | 25900 psi | ASTM D882 |
| 1% Secant Modulus, TD | 190 MPa | 27600 psi | ASTM D882 |
| Hot Tack Strength, Ultimate | 3.80 N | 0.854 lb (f) | |
| Hot Tack Initiation Temperature | 86.1 °C | 187 °F | at 0.5N; ASTM D3706 |
| Heat Seal Strength, Ultimate | 13.6 N | 3.06 lb (f) | |
| Heat Seal Strength Initiation Temperature | 96.1 °C | 205 °F | at 0.5 lb. |
| Optical Properties | Metric | English | Comments |
| Haze | 14 % | 14 % | ASTM D2457 |
| Gloss | 54 % | 54 % | 45°; ASTM D2457 |
| 87 % | 87 % | 60°; ASTM D2457 | |
| Processing Properties | Metric | English | Comments |
| Processing Temperature | 232 °C | 450 °F | |
| Die Opening | 0.203 cm | 0.0799 in | |
| Extruder Size | 6.35 cm | 2.50 in | |