- 熔體流動速率 [g/10min]: 0.5
- 密度 [g/cm3]: 0.917
| Physical Properties | Metric | English | Comments |
|---|---|---|---|
| Density | 0.917 g/cc | 0.0331 lb/in3 | ASTM D4883 |
| Melt Flow | 0.50 g/10 min | 0.50 g/10 min | Condition E; ASTM D1238 |
| Mechanical Properties | Metric | English | Comments |
| Film Elongation at Break, MD | 490 % | 490 % | ASTM D882 |
| Film Elongation at Break, TD | 710 % | 710 % | ASTM D882 |
| Secant Modulus, MD | 0.220 GPa | 31.9 ksi | ASTM D882 |
| Secant Modulus, TD | 0.250 GPa | 36.3 ksi | ASTM D882 |
| Coefficient of Friction | 0.10 | 0.10 | ASTM D1894 |
| Elmendorf Tear Strength, MD | 17.7 g/micron | 450 g/mil | ASTM D1922 |
| Elmendorf Tear Strength, TD | 31.5 g/micron | 800 g/mil | ASTM D1922 |
| Dart Drop | 22.6 g/micron | 574 g/mil | F-50 at 26 in.; ASTM D1709 |
| Dart drop Test | 720 g | 1.59 lb | F-50 at 26 in.; ASTM D1709 |
| Film Tensile Strength at Break, MD | 56.9 MPa | 8250 psi | ASTM D882 |
| Film Tensile Strength at Break, TD | 34.3 MPa | 4970 psi | ASTM D882 |
| Optical Properties | Metric | English | Comments |
| Haze | 16 % | 16 % | ASTM D2457 |
| Gloss | 49 % | 49 % | 45°. ASTM D 2457 |
| 78 % | 78 % | 60°, ASTM D 2457 | |
| Processing Properties | Metric | English | Comments |
| Melt Temperature | 227 - 232 °C | 441 - 450 °F | |