- 熔體流動速率 [g/10min]: 0.9
- 密度 [g/cm3]: 0.918
| Physical Properties | Metric | English | Comments |
|---|---|---|---|
| Density | 0.918 g/cc | 0.0332 lb/in3 | ASTM D4833-89 |
| Melt Flow | 0.90 g/10 min | 0.90 g/10 min | ASTM D1238 |
| Mechanical Properties | Metric | English | Comments |
| Film Elongation at Break, MD | 525 % | 525 % | ASTM D882 |
| Film Elongation at Break, TD | 675 % | 675 % | ASTM D882 |
| Secant Modulus, MD | 0.224 GPa | 32.5 ksi | ASTM D882 |
| Secant Modulus, TD | 0.276 GPa | 40.0 ksi | ASTM D882 |
| Coefficient of Friction | 0.20 | 0.20 | ASTM D1894 |
| Elmendorf Tear Strength, MD | 5.90 g/micron | 150 g/mil | Orientation not specified; ASTM D1922 |
| Elmendorf Tear Strength, TD | 22.6 g/micron | 574 g/mil | ASTM D1922 |
| Dart Drop | 2.40 g/micron | 61.0 g/mil | F-50 at 26 in.; ASTM D1709 |
| Dart drop Test | 75.0 g | 0.165 lb | F-50 at 26 in.; ASTM D1709 |
| Film Tensile Strength at Break, MD | 35.7 MPa | 5180 psi | ASTM D882 |
| Film Tensile Strength at Break, TD | 21.4 MPa | 3100 psi | ASTM D882 |
| Optical Properties | Metric | English | Comments |
| Haze | 12 % | 12 % | ASTM D2457 |
| Gloss | 60 % | 60 % | 45°, ASTM D 2457 |
| 90 % | 90 % | 60°, ASTM D 2457 | |
| Processing Properties | Metric | English | Comments |
| Melt Temperature | 220 °C | 428 °F | |