- 熔體流動速率 [g/10min]: 0.9
- 密度 [g/cm3]: 0.918
| Physical Properties | Metric | English | Comments |
|---|---|---|---|
| Density | 0.918 g/cc | 0.0332 lb/in3 | ASTM D4833-89 |
| Melt Flow | 0.90 g/10 min | 0.90 g/10 min | ASTM D1238 |
| Mechanical Properties | Metric | English | Comments |
| Film Elongation at Break, MD | 500 % | 500 % | ASTM D882 |
| Film Elongation at Break, TD | 640 % | 640 % | ASTM D882 |
| Secant Modulus, MD | 0.255 GPa | 37.0 ksi | ASTM D882 |
| Secant Modulus, TD | 0.337 GPa | 48.9 ksi | ASTM D882 |
| Coefficient of Friction | 0.20 | 0.20 | ASTM D1894 |
| Elmendorf Tear Strength, MD | 16.5 g/micron | 419 g/mil | Orientation not specified; ASTM D1922 |
| Elmendorf Tear Strength, TD | 37.8 g/micron | 960 g/mil | ASTM D1922 |
| Dart Drop | 4.10 g/micron | 104 g/mil | F-50 at 26 in.; ASTM D1709 |
| Dart drop Test | 130 g | 0.287 lb | F-50 at 26 in.; ASTM D1709 |
| Film Tensile Strength at Break, MD | 40.8 MPa | 5920 psi | ASTM D882 |
| Film Tensile Strength at Break, TD | 26.5 MPa | 3840 psi | ASTM D882 |
| Optical Properties | Metric | English | Comments |
| Haze | 14 % | 14 % | ASTM D2457 |
| Gloss | 50 % | 50 % | 45°, ASTM D 2457 |
| 90 % | 90 % | 60°, ASTM D 2457 | |
| Processing Properties | Metric | English | Comments |
| Melt Temperature | 220 °C | 428 °F | |