- 熔體流動速率 [g/10min]: 0.9
- 密度 [g/cm3]: 0.918
| Physical Properties | Metric | English | Comments |
|---|---|---|---|
| Density | 0.918 g/cc | 0.0332 lb/in3 | ASTM D4833-89 |
| Melt Flow | 0.90 g/10 min | 0.90 g/10 min | ASTM D1238 |
| Mechanical Properties | Metric | English | Comments |
| Film Elongation at Break, MD | 560 % | 560 % | ASTM D882 |
| Film Elongation at Break, TD | 770 % | 770 % | ASTM D882 |
| Secant Modulus, MD | 0.260 GPa | 37.7 ksi | ASTM D882 |
| Secant Modulus, TD | 0.327 GPa | 47.4 ksi | ASTM D882 |
| Elmendorf Tear Strength, MD | 16.5 g/micron | 419 g/mil | Orientation not specified; ASTM D1922 |
| Elmendorf Tear Strength, TD | 33.1 g/micron | 841 g/mil | ASTM D1922 |
| Dart Drop | 4.70 g/micron | 119 g/mil | F-50 at 26 in.; ASTM D1709 |
| Dart drop Test | 150 g | 0.331 lb | F-50 at 26 in.; ASTM D1709 |
| Film Tensile Strength at Break, MD | 54.1 MPa | 7850 psi | ASTM D882 |
| Film Tensile Strength at Break, TD | 44.9 MPa | 6510 psi | ASTM D882 |
| Optical Properties | Metric | English | Comments |
| Haze | 11 % | 11 % | ASTM D2457 |
| Gloss | 60 % | 60 % | 45°, ASTM D 2457 |
| 100 % | 100 % | 60°, ASTM D 2457 | |
| Processing Properties | Metric | English | Comments |
| Melt Temperature | 220 °C | 428 °F | |