- 熔體流動速率 [g/10min]: 0.85
- 密度 [g/cm3]: 0.917
| Physical Properties | Metric | English | Comments |
|---|---|---|---|
| Density | 0.917 g/cc | 0.0331 lb/in3 | ASTM D4883 |
| Melt Flow | 0.85 g/10 min | 0.85 g/10 min | Condition E; ASTM D1238 |
| Mechanical Properties | Metric | English | Comments |
| Film Elongation at Break, MD | 580 % | 580 % | ASTM D882 |
| Film Elongation at Break, TD | 710 % | 710 % | ASTM D882 |
| Secant Modulus, MD | 0.200 GPa | 29.0 ksi | ASTM D882 |
| Secant Modulus, TD | 0.240 GPa | 34.8 ksi | ASTM D882 |
| Coefficient of Friction | 1.5 | 1.5 | ASTM D1894 |
| Elmendorf Tear Strength, MD | 20.5 g/micron | 520 g/mil | ASTM D1922 |
| Elmendorf Tear Strength, TD | 26.0 g/micron | 660 g/mil | ASTM D1922 |
| Dart Drop | 11.6 g/micron | 295 g/mil | F-50 at 26 in.; ASTM D1709 |
| Dart drop Test | 370 g | 0.816 lb | F-50 at 26 in.; ASTM D1709 |
| Film Tensile Strength at Break, MD | 55.9 MPa | 8110 psi | ASTM D882 |
| Film Tensile Strength at Break, TD | 44.1 MPa | 6400 psi | ASTM D882 |
| Optical Properties | Metric | English | Comments |
| Haze | 14 % | 14 % | ASTM D2457 |
| Gloss | 54 % | 54 % | 45°. ASTM D 2457 |
| 87 % | 87 % | 60°, ASTM D 2457 | |
| Processing Properties | Metric | English | Comments |
| Melt Temperature | 227 - 232 °C | 441 - 450 °F | |