- 密度 [g/cm3]: 1.56
- 缺口沖擊強度: 0.854
- 拉伸強度 [MPa]: 155.0
- 彎曲模量 [MPa]: 8.96
| Physical Properties | Metric | English | Comments |
|---|---|---|---|
| Density | 1.56 g/cc | 0.0564 lb/in3 | ASTM D792 |
| Linear Mold Shrinkage, Flow | 0.0020 cm/cm @Thickness 3.17 mm | 0.0020 in/in @Thickness 0.125 in | ASTM D955 |
| Mechanical Properties | Metric | English | Comments |
| Tensile Strength, Yield | 155 MPa | 22500 psi | ASTM D638 |
| Elongation at Break | 2.5 % | 2.5 % | ASTM D638 |
| Flexural Strength | 248 MPa | 36000 psi | ASTM D790 |
| Flexural Modulus | 8.96 GPa | 1300 ksi | ASTM D790 |
| Izod Impact, Notched | 0.854 J/cm @Thickness 3.17 mm | 1.60 ft-lb/in @Thickness 0.125 in | ASTM D256 |
| Thermal Properties | Metric | English | Comments |
| Melting Point | 254 °C | 489 °F | |
| Deflection Temperature at 1.8 MPa (264 psi) | 224 °C | 435 °F | Unannealed; ASTM D648 |
| Flammability, UL94 | HB | HB | |