- 密度 [g/cm3]: 2.68
- 吸水率 [%]: 0.1
- 缺口沖擊強(qiáng)度: 0.481
- 拉伸強(qiáng)度 [MPa]: 79.3
- 彎曲模量 [MPa]: 5.86
- 硬度: 118.0
| Physical Properties | Metric | English | Comments |
|---|---|---|---|
| Density | 2.68 g/cc | 0.0968 lb/in3 | ASTM D792 |
| Water Absorption | 0.10 % @Time 86400 sec | 0.10 % @Time 24.0 hour | ASTM D570 |
| Linear Mold Shrinkage, Flow | 0.0040 cm/cm @Thickness 3.17 mm | 0.0040 in/in @Thickness 0.125 in | ASTM D955 |
| Mechanical Properties | Metric | English | Comments |
| Hardness, Rockwell R | 118 | 118 | ASTM D785 |
| Tensile Strength, Yield | 79.3 MPa | 11500 psi | ASTM D638 |
| Elongation at Break | 3.0 % | 3.0 % | ASTM D638 |
| Flexural Strength | 117 MPa | 17000 psi | ASTM D790 |
| Flexural Modulus | 5.86 GPa | 850 ksi | ASTM D790 |
| Izod Impact, Notched | 0.481 J/cm @Thickness 3.17 mm | 0.900 ft-lb/in @Thickness 0.125 in | ASTM D256 |
| Electrical Properties | Metric | English | Comments |
| Volume Resistivity | 1.00e+13 - 1.00e+14 ohm-cm | 1.00e+13 - 1.00e+14 ohm-cm | ASTM D257 |
- 關(guān)鍵詞:
- PET
- 供應(yīng)
- TP Composites HiFill? PET 0268 B1