- 密度 [g/cm3]: 1.8
- 吸水率 [%]: 0.03
- 缺口沖擊強度: 1.12
- 拉伸強度 [MPa]: 193.0
- 彎曲模量 [MPa]: 17.2
- 硬度: 121.0
| Physical Properties | Metric | English | Comments |
|---|---|---|---|
| Density | 1.80 g/cc | 0.0650 lb/in3 | ASTM D792 |
| Water Absorption | 0.030 % @Time 86400 sec | 0.030 % @Time 24.0 hour | ASTM D570 |
| Linear Mold Shrinkage, Flow | 0.0020 cm/cm @Thickness 3.17 mm | 0.0020 in/in @Thickness 0.125 in | ASTM D955 |
| Mechanical Properties | Metric | English | Comments |
| Hardness, Rockwell R | 121 | 121 | ASTM D785 |
| Tensile Strength, Yield | 193 MPa | 28000 psi | ASTM D638 |
| Elongation at Break | 1.5 % | 1.5 % | ASTM D638 |
| Flexural Strength | 303 MPa | 44000 psi | ASTM D790 |
| Flexural Modulus | 17.2 GPa | 2500 ksi | ASTM D790 |
| Izod Impact, Notched | 1.12 J/cm @Thickness 3.17 mm | 2.10 ft-lb/in @Thickness 0.125 in | ASTM D256 |
| Electrical Properties | Metric | English | Comments |
| Volume Resistivity | 1.00e+16 ohm-cm | 1.00e+16 ohm-cm | ASTM D257 |
| Dielectric Strength | 17.7 kV/mm | 450 kV/in | Method A (Short-Time); ASTM D149 |
| Thermal Properties | Metric | English | Comments |
| CTE, linear, Parallel to Flow | 16.2 μm/m-°C | 9.00 μin/in-°F | ASTM D696 |
| Melting Point | 254 °C | 489 °F | |
| Deflection Temperature at 1.8 MPa (264 psi) | 229 °C | 445 °F | Unannealed; ASTM D648 |