- 密度 [g/cm3]: 1.59
- 吸水率 [%]: 0.06
- 缺口沖擊強度: 0.57
- 彎曲模量 [MPa]: 7.10
- 熱變形溫度 [℃]: 240.0
| Physical Properties | Metric | English | Comments |
|---|---|---|---|
| Density | 1.59 g/cc | 0.0574 lb/in3 | ASTM D792 |
| Water Absorption | 0.060 % | 0.060 % | ASTM D570 |
| Linear Mold Shrinkage, Flow | 0.0040 cm/cm | 0.0040 in/in | MD |
| Linear Mold Shrinkage, Transverse | 0.0080 cm/cm | 0.0080 in/in | |
| Mechanical Properties | Metric | English | Comments |
| Hardness, Rockwell M | 90 | 90 | ASTM D785 |
| Tensile Strength at Break | 100 MPa | 14500 psi | ASTM D638 |
| Elongation at Break | 2.2 % | 2.2 % | ASTM D638 |
| Flexural Strength | 145 MPa | 21000 psi | ASTM D790 |
| Flexural Modulus | 7.10 GPa | 1030 ksi | ASTM D790 |
| Izod Impact, Notched | 0.570 J/cm | 1.07 ft-lb/in | ASTM D256 |
| Taber Abrasion, mg/1000 Cycles | 35 | 35 | CS-17; ASTM D1044 |
| Electrical Properties | Metric | English | Comments |
| Volume Resistivity | 1.00e+16 ohm-cm | 1.00e+16 ohm-cm | ASTM D257 |
| Dielectric Strength | 25.0 kV/mm @Thickness 2.00 mm | 635 kV/in @Thickness 0.0787 in | ASTM D149 |
| Arc Resistance | 139 sec | 139 sec | UL recognition value, tungsten electrode; ASTM D495 |
| Comparative Tracking Index | 250 - 399 V | 250 - 399 V | IEC Pub1.112, class 2; IEC Method |
| Thermal Properties | Metric | English | Comments |
| CTE, linear | 40.0 μm/m-°C @Temperature 20.0 °C | 22.2 μin/in-°F @Temperature 68.0 °F | ASTM D696 |
| Melting Point | 255 °C | 491 °F | By DSC |
| Maximum Service Temperature, Air | 120 °C | 248 °F | Thermal index; ASTM UL746B |
| 225 °C | 437 °F | Ball pressure temperature; IEC Method | |
| Deflection Temperature at 0.46 MPa (66 psi) | 240 °C | 464 °F | ASTM D648 |
| Deflection Temperature at 1.8 MPa (264 psi) | 210 °C | 410 °F | ASTM D648 |
| Flammability, UL94 | HB @Thickness 0.7937 mm | HB @Thickness 0.03125 in | |
| Processing Properties | Metric | English | Comments |
| Melt Temperature | 255 - 265 °C | 491 - 509 °F | |
| Mold Temperature | 90.0 - 120 °C | 194 - 248 °F | |