- 密度 [g/cm3]: 1.54
- 吸水率 [%]: 0.08
- 缺口沖擊強(qiáng)度: 0.801
- 拉伸強(qiáng)度 [MPa]: 34.5
- 斷裂伸長(zhǎng)率 [%]: 6.89
- 彎曲模量 [MPa]: 2.07
- 硬度: 120.0
- 熱變形溫度 [℃]: 241.0
| Physical Properties | Metric | English | Comments |
|---|---|---|---|
| Density | 1.54 g/cc | 0.0556 lb/in3 | ASTM D792 |
| Water Absorption | 0.080 % @Time 86400 sec | 0.080 % @Time 24.0 hour | ASTM D570 |
| Linear Mold Shrinkage, Flow | 0.0060 cm/cm @Thickness 3.17 mm | 0.0060 in/in @Thickness 0.125 in | ASTM D955 |
| Mechanical Properties | Metric | English | Comments |
| Hardness, Rockwell R | 120 | 120 | ASTM D785 |
| Tensile Strength, Yield | 34.5 MPa | 5000 psi | ASTM D638 |
| Elongation at Break | 5.0 % | 5.0 % | ASTM D638 |
| Flexural Yield Strength | 6.89 MPa | 1000 psi | ASTM D790 |
| Flexural Modulus | 2.07 GPa | 300 ksi | ASTM D790 |
| Izod Impact, Notched | 0.801 J/cm @Thickness 3.17 mm | 1.50 ft-lb/in @Thickness 0.125 in | ASTM D256 |
| Electrical Properties | Metric | English | Comments |
| Volume Resistivity | 1.00e+14 ohm-cm | 1.00e+14 ohm-cm | ASTM D257 |
| Dielectric Strength | 16.1 kV/mm | 410 kV/in | Method A (Short-Time); ASTM D149 |
| Thermal Properties | Metric | English | Comments |
| CTE, linear, Parallel to Flow | 12.6 μm/m-°C | 7.00 μin/in-°F | ASTM D696 |
| Deflection Temperature at 0.46 MPa (66 psi) | 241 °C | 465 °F | Unannealed; ASTM D648 |
| Deflection Temperature at 1.8 MPa (264 psi) | 213 °C | 415 °F | Unannealed; ASTM D648 |
| Flammability, UL94 | V-0 | V-0 | |