- 熔體流動(dòng)速率 [g/10min]: 33.0
- 缺口沖擊強(qiáng)度: 1.06
- 拉伸強(qiáng)度 [MPa]: 145.0
- 彎曲模量 [MPa]: 10.68
- 熱變形溫度 [℃]: 215.0
| Physical Properties | Metric | English | Comments |
|---|---|---|---|
| Specific Gravity | 1.64 g/cc | 1.64 g/cc | ASTM D792 |
| Linear Mold Shrinkage, Flow | 0.0020 - 0.0050 cm/cm @Thickness 3.20 mm | 0.0020 - 0.0050 in/in @Thickness 0.126 in | SABIC Method |
| Linear Mold Shrinkage, Transverse | 0.0050 - 0.0080 cm/cm @Thickness 3.20 mm | 0.0050 - 0.0080 in/in @Thickness 0.126 in | SABIC Method |
| Melt Flow | 33 g/10 min @Load 5.00 kg, Temperature 266 °C | 33 g/10 min @Load 11.0 lb, Temperature 511 °F | ASTM D1238 |
| Melt Index of Compound | 22 g/10 min @Load 5.00 kg, Temperature 265 °C | 22 g/10 min @Load 11.0 lb, Temperature 509 °F | MVR [cm^3/10 min]; ISO 1133 |
| Mechanical Properties | Metric | English | Comments |
| Tensile Strength at Break | 145 MPa | 21000 psi | Type I, 5 mm/min; ASTM D638 |
| Tensile Strength, Yield | 145 MPa | 21000 psi | Type I, 5 mm/min; ASTM D638 |
| Elongation at Break | 2.2 % | 2.2 % | Type I, 5 mm/min; ASTM D638 |
| Elongation at Yield | 2.2 % | 2.2 % | Type I, 5 mm/min; ASTM D638 |
| Tensile Modulus | 12.75 GPa | 1849 ksi | 5 mm/min; ASTM D638 |
| Flexural Strength | 220 MPa | 31900 psi | brk, 1.3 mm/min, 50 mm span; ASTM D790 |
| Flexural Modulus | 10.68 GPa | 1549 ksi | 1.3 mm/min, 50 mm span; ASTM D790 |
| Izod Impact, Notched | 1.06 J/cm | 1.99 ft-lb/in | ASTM D256 |
| Izod Impact, Unnotched | 8.27 J/cm | 15.5 ft-lb/in | ASTM D4812 |
| Dart Drop, Total Energy | 7.00 J @Temperature 23.0 °C | 5.16 ft-lb @Temperature 73.4 °F | ASTM D3763 |
| Thermal Properties | Metric | English | Comments |
| CTE, linear, Parallel to Flow | 14.4 μm/m-°C @Temperature -40.0 - 40.0 °C | 8.00 μin/in-°F @Temperature -40.0 - 104 °F | ASTM E 831 |
| CTE, linear, Transverse to Flow | 73.8 μm/m-°C @Temperature -40.0 - 40.0 °C | 41.0 μin/in-°F @Temperature -40.0 - 104 °F | ASTM E 831 |
| Deflection Temperature at 0.46 MPa (66 psi) | 215 °C @Thickness 3.20 mm | 419 °F @Thickness 0.126 in | unannealed; ASTM D648 |
| Deflection Temperature at 1.8 MPa (264 psi) | 193 °C @Thickness 3.20 mm | 379 °F @Thickness 0.126 in | unannealed; ASTM D648 |
| Vicat Softening Point | 221 °C | 430 °F | Rate B/50; ASTM D1525 |