- 密度 [g/cm3]: 1.76
- 吸水率 [%]: 0.16
- 拉伸強度 [MPa]: 175.0
- 斷裂伸長率 [%]: 255
- 彎曲模量 [MPa]: 16.0
| Physical Properties | Metric | English | Comments |
|---|---|---|---|
| Density | 1.76 g/cc | 0.0636 lb/in3 | ISO 1183 |
| Moisture Absorption | 0.0500 % | 0.0500 % | 23°C / 50% RH; ISO 62 |
| Water Absorption at Saturation | 0.16 % | 0.16 % | ISO 62 |
| Linear Mold Shrinkage, Flow | 0.0010 - 0.0050 cm/cm | 0.0010 - 0.0050 in/in | on Tensile Bar; SABIC Method |
| Linear Mold Shrinkage, Transverse | 0.0020 - 0.0060 cm/cm | 0.0020 - 0.0060 in/in | on Tensile Bar; SABIC Method |
| Melt Index of Compound | 7.0 g/10 min @Load 2.16 kg, Temperature 265 °C | 7.0 g/10 min @Load 4.76 lb, Temperature 509 °F | MVR [cm^3/10 min]; ISO 1133 |
| Mechanical Properties | Metric | English | Comments |
| Tensile Strength at Break | 175 MPa | 25400 psi | 5 mm/min; ISO 527 |
| Tensile Strength, Yield | 175 MPa | 25400 psi | 5 mm/min; ISO 527 |
| Elongation at Break | 1.5 % | 1.5 % | 5 mm/min; ISO 527 |
| Elongation at Yield | 1.5 % | 1.5 % | 5 mm/min; ISO 527 |
| Tensile Modulus | 17.5 GPa | 2540 ksi | 1 mm/min; ISO 527 |
| Flexural Yield Strength | 255 MPa | 37000 psi | 2 mm/min; ISO 178 |
| Flexural Modulus | 16.0 GPa | 2320 ksi | 2 mm/min; ISO 178 |
| Izod Impact, Unnotched (ISO) | 40.0 kJ/m2 | 19.0 ft-lb/in2 | 80*10*4; ISO 180/1U |
| 40.0 kJ/m2 @Temperature -30.0 °C | 19.0 ft-lb/in2 @Temperature -22.0 °F | 80*10*4; ISO 180/1U | |
| Charpy Impact, Notched | 1.10 J/cm2 | 5.23 ft-lb/in2 | Edgew 80*10*4 sp=62mm; ISO 179/1eA |
| Thermal Properties | Metric | English | Comments |
| CTE, linear, Parallel to Flow | 15.0 μm/m-°C @Temperature 23.0 - 80.0 °C | 8.33 μin/in-°F @Temperature 73.4 - 176 °F | ISO 11359-2 |
| CTE, linear, Transverse to Flow | 72.0 μm/m-°C @Temperature 23.0 - 80.0 °C | 40.0 μin/in-°F @Temperature 73.4 - 176 °F | ISO 11359-2 |
| Deflection Temperature at 1.8 MPa (264 psi) | 206 °C | 403 °F | Edgew 120*10*4 sp=100mm; ISO 75/Ae |
| Vicat Softening Point | 210 °C | 410 °F | Rate B/120; ISO 306 |
| 212 °C | 414 °F | Rate B/50; ISO 306 | |