- 熔體流動速率 [g/10min]: 5.0
- 密度 [g/cm3]: 1.58
- 吸水率 [%]: 0.3
- 缺口沖擊強度: 0.6
- 拉伸強度 [MPa]: 103.0
- 斷裂伸長率 [%]: 145
- 彎曲模量 [MPa]: 10.0
- 硬度: 118.0
- 熱變形溫度 [℃]: 215.0
| Physical Properties | Metric | English | Comments | ||
|---|---|---|---|---|---|
| Specific Gravity | 1.58 g/cc | 1.58 g/cc | ASTM D792 | ||
| Density | 1.58 g/cc | 0.0571 lb/in3 | ISO 1183 | ||
| Filler Content | 30 % | 30 % | ASTM D229 | ||
| Moisture Absorption | 0.0500 % | 0.0500 % | 23°C / 50% RH; ISO 62 | ||
| Water Absorption at Saturation | 0.30 % | 0.30 % | ISO 62 | ||
| Viscosity | 155000 cP | 155000 cP | Melt Viscosity, 260°C, 1500 sec-1; ISO 11443 | ||
| Linear Mold Shrinkage, Flow | 0.0030 - 0.0040 cm/cm | 0.0030 - 0.0040 in/in | on Tensile Bar; SABIC Method | ||
| Melt Flow | 5.0 g/10 min @Load 2.16 kg, Temperature 265 °C | 5.0 g/10 min @Load 4.76 lb, Temperature 509 °F | ASTM D1238 | ||
| 11 g/10 min @Load 5.00 kg, Temperature 250 °C | 11 g/10 min @Load 11.0 lb, Temperature 482 °F | ISO 1133 | |||
| 11 g/10 min @Load 5.00 kg, Temperature 250 °C | 11 g/10 min @Load 11.0 lb, Temperature 482 °F | ASTM D1238 | |||
| Melt Index of Compound | 10 g/10 min @Load 5.00 kg, Temperature 250 °C | 10 g/10 min @Load 11.0 lb, Temperature 482 °F | MVR [cm^3/10 min]; ASTM D1238 | ||
| 25 g/10 min @Load 5.00 kg, Temperature 265 °C | 25 g/10 min @Load 11.0 lb, Temperature 509 °F | MVR [cm^3/10 min]; ISO 1133 | |||
| Mechanical Properties | Metric | English | Comments | ||
| Hardness, Rockwell R | 118 | 118 | ISO 2039-2 | ||
| Hardness, H358/30 | 166 MPa | 24100 psi | ISO 2039-1 | ||
| Tensile Strength at Break | 103 MPa | 14900 psi | Type I, 5 mm/min; ASTM D638 | ||
| 105 MPa | 15200 psi | 5 mm/min; ISO 527 | |||
| Tensile Strength, Yield | 103 MPa | 14900 psi | Type I, 5 mm/min; ASTM D638 | ||
| 105 MPa | 15200 psi | 5 mm/min; ISO 527 | |||
| Elongation at Break | 2.0 % | 2.0 % | Type I, 5 mm/min; ASTM D638 | ||
| 2.0 % | 2.0 % | 5 mm/min; ISO 527 | |||
| 2.0 % | 2.0 % | Flexural Strain, break, 2 mm/min; ISO 178 | |||
| Elongation at Yield | 1.0 % | 1.0 % | Type I, 5 mm/min; ASTM D638 | ||
| 1.0 % | 1.0 % | 5 mm/min; ISO 527 | |||
| Tensile Modulus | 12.0 GPa | 1740 ksi | 5 mm/min; ASTM D638 | ||
| 12.0 GPa | 1740 ksi | 1 mm/min; ISO 527 | |||
| Flexural Strength | 145 MPa | 21000 psi | brk, 1.3 mm/min, 50 mm span; ASTM D790 | ||
| 165 MPa | 23900 psi | break, 2 mm/min; ISO 178 | |||
| Flexural Yield Strength | 145 MPa | 21000 psi | 1.3 mm/min, 50 mm span; ASTM D790 | ||
| 165 MPa | 23900 psi | 2 mm/min; ISO 178 | |||
| Flexural Modulus | 10.0 GPa | 1450 ksi | 1.3 mm/min, 50 mm span; ASTM D790 | ||
| 10.0 GPa | 1450 ksi | 2 mm/min; ISO 178 | |||
| Izod Impact, Notched | 0.600 J/cm | 1.12 ft-lb/in | ASTM D256 | ||
| 0.600 J/cm @Temperature 0.000 °C | 1.12 ft-lb/in @Temperature 32.0 °F | ASTM D256 | |||
| 0.600 J/cm @Temperature -30.0 °C | 1.12 ft-lb/in @Temperature -22.0 °F | ASTM D256 | |||
| Izod Impact, Unnotched | 4.50 J/cm | 8.43 ft-lb/in | ASTM D4812 | ||
| 4.00 J/cm @Temperature -30.0 °C | 7.49 ft-lb/in @Temperature -22.0 °F | ASTM D4812 | |||
| Izod Impact, Notched (ISO) | 7.00 kJ/m2 | 3.33 ft-lb/in2 | 80*10*4; ISO 180/1A | ||
| 7.00 kJ/m2 @Temperature 0.000 °C | 3.33 ft-lb/in2 @Temperature 32.0 °F | 80*10*4; ISO 180/1A | |||
| 7.00 kJ/m2 @Temperature -30.0 °C | 3.33 ft-lb/in2 @Temperature -22.0 °F | 80*10*4; ISO 180/1A | |||
| Izod Impact, Unnotched (ISO) | 30.0 kJ/m2 | 14.3 ft-lb/in2 | 80*10*4; ISO 180/1U | ||
| 27.0 kJ/m2 @Temperature -30.0 °C | 12.8 ft-lb/in2 @Temperature -22.0 °F | 80*10*4; ISO 180/1U | |||
| Charpy Impact Unnotched | 3.00 J/cm2 | 14.3 ft-lb/in2 | ISO 179/2C | ||
| 3.00 J/cm2 @Temperature -30.0 °C | 14.3 ft-lb/in2 @Temperature -22.0 °F | ISO 179/2C | |||
| Charpy Impact, Notched | 0.500 J/cm2 | 2.38 ft-lb/in2 | Edgew 80*10*4 sp=62mm; ISO 179/1eA | ||
| 0.700 J/cm2 | 3.33 ft-lb/in2 | ISO 179/2C | |||
| 0.700 J/cm2 @Temperature -30.0 °C | 3.33 ft-lb/in2 @Temperature -22.0 °F | ISO 179/2C | |||
| Electrical Properties | Metric | English | Comments | ||
| Volume Resistivity | 1.00e+15 ohm-cm | 1.00e+15 ohm-cm | ASTM D257 | ||
| 1.00e+15 ohm-cm | 1.00e+15 ohm-cm | IEC 60093 | |||
| Surface Resistance | >= 1.00e+15 ohm | >= 1.00e+15 ohm | ROA; IEC 60093 | ||
| Dielectric Constant | 3.6 @Frequency 1.00e+6 Hz | 3.6 @Frequency 1.00e+6 Hz | ASTM D150 | ||
| 3.6 @Frequency 1.00e+6 Hz | 3.6 @Frequency 1.00e+6 Hz | IEC 60250 | |||
| Dielectric Strength | 8.00 kV/mm @Thickness 3.20 mm | 203 kV/in @Thickness 0.126 in | in oil; IEC 60243-1 | ||
| 8.00 kV/mm @Thickness 3.20 mm | 203 kV/in @Thickness 0.126 in | in oil; ASTM D149 | |||
| 25.0 kV/mm @Thickness 1.60 mm | 635 kV/in @Thickness 0.0630 in | in oil; IEC 60243-1 | |||
| 25.0 kV/mm @Thickness 1.60 mm | 635 kV/in @Thickness 0.0630 in | in oil; ASTM D149 | |||
| 35.0 kV/mm @Thickness 0.800 mm | 889 kV/in @Thickness 0.0315 in | in oil; ASTM D149 | |||
| 35.0 kV/mm @Thickness 0.800 mm | 889 kV/in @Thickness 0.0315 in | in oil; IEC 60243-1 | |||
| Dissipation Factor | 0.012 @Frequency 1.00e+6 Hz | 0.012 @Frequency 1.00e+6 Hz | ASTM D150 | ||
| 0.012 @Frequency 1.00e+6 Hz | 0.012 @Frequency 1.00e+6 Hz | IEC 60250 | |||
| Comparative Tracking Index | 250 - 400 V | 250 - 400 V | UL 746A | ||
| 425 V | 425 V | IEC 60112 | |||
| Hot Wire Ignition, HWI | >= 120 sec | >= 120 sec | UL 746A | ||
| High Amp Arc Ignition, HAI | >= 120 arcs | >= 120 arcs | UL 746A | ||
| Thermal Properties | Metric | English | Comments | ||
| CTE, linear, Parallel to Flow | 19.0 μm/m-°C @Temperature -40.0 - 40.0 °C | 10.6 μin/in-°F @Temperature -40.0 - 104 °F | ISO 11359-2 | ||
| 21.0 μm/m-°C @Temperature 23.0 - 150 °C | 11.7 μin/in-°F @Temperature 73.4 - 302 °F | ISO 11359-2 | |||
| CTE, linear, Transverse to Flow | 56.0 μm/m-°C @Temperature -40.0 - 40.0 °C | 31.1 μin/in-°F @Temperature -40.0 - 104 °F | ISO 11359-2 | ||
| 140 μm/m-°C @Temperature 23.0 - 150 °C | 77.8 μin/in-°F @Temperature 73.4 - 302 °F | ISO 11359-2 | |||
| Deflection Temperature at 0.46 MPa (66 psi) | 215 °C | 419 °F | Flatw 80*10*4 sp=64mm; ISO 75/Bf | ||
| 210 °C @Thickness 3.20 mm | 410 °F @Thickness 0.126 in | unannealed; ASTM D648 | |||
| Deflection Temperature at 1.8 MPa (264 psi) | 180 °C | 356 °F | Flatw 80*10*4 sp=64mm; ISO 75/Af | ||
| 196 °C @Thickness 3.20 mm | 385 °F @Thickness 0.126 in | unannealed; ASTM D648 | |||
| Vicat Softening Point | 196 °C | 385 °F | Rate B/50; ASTM D1525 | ||
| 201 °C | 394 °F | Rate B/120; ISO 306 | |||
| 203 °C | 397 °F | Rate B/50; ISO 306 | |||
| 215 °C | 419 °F | Rate A/50; ISO 306 | |||
| 220 °C | 428 °F | Rate A/50; ASTM D1525 | |||
| UL RTI, Electrical | 75.0 °C | 167 °F | UL 746B | ||
| UL RTI, Mechanical with Impact | 75.0 °C | 167 °F | UL 746B | ||
| UL RTI, Mechanical without Impact | 75.0 °C | 167 °F | UL 746B | ||
| Flammability, UL94 | V-0 @Thickness 1.50 mm | V-0 @Thickness 0.0591 in | UL 94 | ||
| 5VA @Thickness 3.00 mm | 5VA @Thickness 0.118 in | UL 94 | |||
| Glow Wire Test | 750 °C | 1380 °F | IEC 60695-2-13 | ||
| 775 °C | 1430 °F | IEC 60695-2-13 | |||
| 825 °C | 1520 °F | IEC 60695-2-13 | |||
| 960 °C @Thickness 1.50 - 3.00 mm | 1760 °F @Thickness 0.0591 - 0.118 in | IEC 60695-2-12 | |||
| Descriptive Properties | |||||
| Ball Pressure Test, 125°C +/- 2°C | PASSES | IEC 60695-10-2 | |||