- 密度 [g/cm3]: 1.81
- 缺口沖擊強度: 0.03
- 斷裂伸長率 [%]: 100
- 彎曲模量 [MPa]: 3.90
| Physical Properties | Metric | English | Comments | ||
|---|---|---|---|---|---|
| Density | 1.81 g/cc | 0.0654 lb/in3 | ISO 1183 | ||
| Linear Mold Shrinkage, Flow | 0.012 - 0.019 cm/cm @Thickness 3.20 mm | 0.012 - 0.019 in/in @Thickness 0.126 in | SABIC Method | ||
| Melt Index of Compound | 21 g/10 min @Load 1.20 kg, Temperature 265 °C | 21 g/10 min @Load 2.65 lb, Temperature 509 °F | MVR [cm^3/10 min]; ISO 1133 | ||
| Mechanical Properties | Metric | English | Comments | ||
| Hardness, H358/30 | 140 MPa | 20300 psi | ISO 2039-1 | ||
| Tensile Strength at Break | 60.0 MPa | 8700 psi | 5 mm/min; ISO 527 | ||
| Elongation at Break | 3.0 % | 3.0 % | 5 mm/min; ISO 527 | ||
| Tensile Modulus | 4.20 GPa | 609 ksi | 1 mm/min; ISO 527 | ||
| Flexural Yield Strength | 100 MPa | 14500 psi | 2 mm/min; ISO 178 | ||
| Flexural Modulus | 3.90 GPa | 566 ksi | 2 mm/min; ISO 178 | ||
| Izod Impact, Notched | 0.0300 J/cm | 0.0562 ft-lb/in | ASTM D256 | ||
| 0.0300 J/cm @Temperature -30.0 °C | 0.0562 ft-lb/in @Temperature -22.0 °F | ASTM D256 | |||
| Izod Impact, Notched (ISO) | 3.00 kJ/m2 | 1.43 ft-lb/in2 | 80*10*4; ISO 180/1A | ||
| 3.00 kJ/m2 @Temperature -30.0 °C | 1.43 ft-lb/in2 @Temperature -22.0 °F | 80*10*4; ISO 180/1A | |||
| Charpy Impact, Notched | 0.200 J/cm2 | 0.952 ft-lb/in2 | Edgew 80*10*4 sp=62mm; ISO 179/1eA | ||
| 0.200 J/cm2 @Temperature -30.0 °C | 0.952 ft-lb/in2 @Temperature -22.0 °F | Edgew 80*10*3 sp=62mm; ISO 179/1eA | |||
| Taber Abrasion, mg/1000 Cycles | 74 | 74 | CS-17, 1 kg; SABIC Method | ||
| Electrical Properties | Metric | English | Comments | ||
| Dielectric Constant | 3.6 @Frequency 1.00e+6 Hz | 3.6 @Frequency 1.00e+6 Hz | ASTM D150 | ||
| 3.7 @Frequency 50.0 - 60.0 Hz | 3.7 @Frequency 50.0 - 60.0 Hz | ASTM D150 | |||
| Dissipation Factor | 0.0020 @Frequency 50.0 - 60.0 Hz | 0.0020 @Frequency 50.0 - 60.0 Hz | ASTM D150 | ||
| 0.015 @Frequency 1.00e+6 Hz | 0.015 @Frequency 1.00e+6 Hz | ASTM D150 | |||
| Comparative Tracking Index | 475 V | 475 V | IEC 60112 | ||
| Thermal Properties | Metric | English | Comments | ||
| CTE, linear, Parallel to Flow | 90.0 μm/m-°C @Temperature 23.0 - 80.0 °C | 50.0 μin/in-°F @Temperature 73.4 - 176 °F | ISO 11359-2 | ||
| CTE, linear, Transverse to Flow | 90.0 μm/m-°C @Temperature 23.0 - 80.0 °C | 50.0 μin/in-°F @Temperature 73.4 - 176 °F | ISO 11359-2 | ||
| Deflection Temperature at 1.8 MPa (264 psi) | 65.0 °C @Thickness 3.20 mm | 149 °F @Thickness 0.126 in | unannealed; ASTM D648 | ||
| Vicat Softening Point | 175 °C | 347 °F | Rate B/50; ASTM D1525 | ||
| 175 °C | 347 °F | Rate B/50; ISO 306 | |||
| 175 °C | 347 °F | Rate B/120; ISO 306 | |||
| Flammability, UL94 | HB @Thickness 1.50 mm | HB @Thickness 0.0591 in | UL 94 | ||
| HB @Thickness 3.00 mm | HB @Thickness 0.118 in | UL 94 | |||
| Glow Wire Test | 650 °C @Thickness 3.20 mm | 1200 °F @Thickness 0.126 in | IEC 60695-2-12 | ||
| Descriptive Properties | |||||
| Ball Pressure Test, 125°C +/- 2°C | PASSES | IEC 60695-10-2 | |||