- 密度 [g/cm3]: 1.39
- 吸水率 [%]: 0.5
- 拉伸強度 [MPa]: 90.0
| Physical Properties | Metric | English | Comments | ||
|---|---|---|---|---|---|
| Density | 1.39 g/cc | 0.0502 lb/in3 | ISO 1183-1 | ||
| Moisture Absorption at Equilibrium | 0.25 % @Temperature 23.0 °C | 0.25 % @Temperature 73.4 °F | 50% RH | ||
| Water Absorption at Saturation | 0.50 % @Temperature 23.0 °C | 0.50 % @Temperature 73.4 °F | |||
| Mechanical Properties | Metric | English | Comments | ||
| Hardness, Rockwell M | 96 | 96 | ISO 2039-2 | ||
| Hardness, Shore D | 81 | 81 | DIN 53505 | ||
| Ball Indentation Hardness | 170 MPa | 24700 psi | ISO 2039-1 | ||
| Tensile Strength, Yield | 90.0 MPa | 13100 psi | dry; ISO 527-1/-2 | ||
| 90.0 MPa | 13100 psi | 50% RH; ISO 527-1/-2 | |||
| Elongation at Break | 15 % | 15 % | dry; ISO 527-1/-2 | ||
| 15 % | 15 % | 50% RH; ISO 527-1/-2 | |||
| Creep Strength | 26.0 MPa | 3770 psi | stress leading to 1% elongation; dry; ISO 899-1 | ||
| 26.0 MPa | 3770 psi | stress leading to 1% elongation; 50% RH; ISO 899-1 | |||
| Modulus of Elasticity | 3.50 GPa | 508 ksi | dry | ||
| 3.50 GPa | 508 ksi | 50% RH | |||
| Compressive Yield Strength | 26.0 MPa @Strain 1.00 % | 3770 psi @Strain 1.00 % | dry; ISO 604 | ||
| 51.0 MPa @Strain 2.00 % | 7400 psi @Strain 2.00 % | dry; ISO 604 | |||
| 103 MPa @Strain 5.00 % | 14900 psi @Strain 5.00 % | dry; ISO 604 | |||
| Charpy Impact Unnotched | 5.00 J/cm2 | 23.8 ft-lb/in2 | ISO 179-1/1eU | ||
| >= 5.00 J/cm2 | >= 23.8 ft-lb/in2 | ISO 179 | |||
| Charpy Impact, Notched | 0.200 J/cm2 | 0.952 ft-lb/in2 | ISO 179-1/1eA | ||
| Coefficient of Friction, Dynamic | 0.30 | 0.30 | |||
| Electrical Properties | Metric | English | Comments | ||
| Electrical Resistivity | >= 1.00e+14 ohm-cm | >= 1.00e+14 ohm-cm | dry; IEC 60093 | ||
| >= 1.00e+14 ohm-cm | >= 1.00e+14 ohm-cm | 50% RH; IEC 60093 | |||
| Surface Resistance | >= 1.00e+13 ohm | >= 1.00e+13 ohm | dry; IEC 60093 | ||
| >= 1.00e+13 ohm | >= 1.00e+13 ohm | 50% RH; IEC 60093 | |||
| Dielectric Constant | 3.2 @Frequency 1.00e+6 Hz | 3.2 @Frequency 1.00e+6 Hz | dry; IEC 60250 | ||
| 3.2 @Frequency 1.00e+6 Hz | 3.2 @Frequency 1.00e+6 Hz | 50% RH; IEC 60250 | |||
| 3.4 @Frequency 100 Hz | 3.4 @Frequency 100 Hz | dry; IEC 60250 | |||
| 3.4 @Frequency 100 Hz | 3.4 @Frequency 100 Hz | 50% RH; IEC 60250 | |||
| Dielectric Strength | 22.0 kV/mm | 559 kV/in | dry; IEC 60243-1 | ||
| 22.0 kV/mm | 559 kV/in | 50% RH; IEC 60243-1 | |||
| Dielectric Loss Index | 0.0010 @Frequency 100 Hz | 0.0010 @Frequency 100 Hz | dry; IEC 60250 | ||
| 0.0010 @Frequency 100 Hz | 0.0010 @Frequency 100 Hz | 50% RH; IEC 60250 | |||
| 0.014 @Frequency 1.00e+6 Hz | 0.014 @Frequency 1.00e+6 Hz | dry; IEC 60250 | |||
| 0.014 @Frequency 1.00e+6 Hz | 0.014 @Frequency 1.00e+6 Hz | 50% RH; IEC 60250 | |||
| Thermal Properties | Metric | English | Comments | ||
| CTE, linear | 60.0 μm/m-°C @Temperature 23.0 - 60.0 °C | 33.3 μin/in-°F @Temperature 73.4 - 140 °F | |||
| 80.0 μm/m-°C @Temperature 23.0 - 100 °C | 44.4 μin/in-°F @Temperature 73.4 - 212 °F | ||||
| Melting Point | 245 °C | 473 °F | ISO 11357-1 | ||
| Maximum Service Temperature, Air | 100 °C @Time 7.20e+7 sec | 212 °F @Time 20000 hour | |||
| 115 °C @Time 1.80e+7 sec | 239 °F @Time 5000 hour | ||||
| 160 °C @Time <=86400 sec | 320 °F @Time <=24.0 hour | ||||
| Minimum Service Temperature, Air | -20.0 °C | -4.00 °F | |||
| Glass Transition Temp, Tg | 70.0 °C | 158 °F | ISO 11357-1 | ||
| Flammability, UL94 | HB | HB | |||
| Compliance Properties | Metric | English | Comments | ||
| European Food 1935/2004 | Yes | Yes | |||
| FDA | Yes | Yes | |||
| Descriptive Properties | |||||
| Color | Natural/Black | ||||