| Physical Properties | Metric | English | Comments | ||
|---|---|---|---|---|---|
| Linear Mold Shrinkage | 0.010 cm/cm @Temperature 150 °C, Time 900 sec | 0.010 in/in @Temperature 302 °F, Time 0.250 hour | DIN 40634 | ||
| Linear Mold Shrinkage, Transverse | 0.010 cm/cm @Temperature 150 °C, Time 900 sec | 0.010 in/in @Temperature 302 °F, Time 0.250 hour | DIN 40634 | ||
| Mechanical Properties | Metric | English | Comments | ||
| Film Tensile Strength at Yield, MD | 200 MPa | 29000 psi | Test speed 100%/min.; 50% r.h.; ISO 527-1, ISO 527-3; Sample type 2 | ||
| Film Tensile Strength at Yield, TD | 200 MPa | 29000 psi | Test speed 100%/min.; 50% r.h.; ISO 527-1, ISO 527-3; Sample type 2 | ||
| Film Elongation at Break, MD | >= 200 % | >= 200 % | Test speed 100%/min.; 50% r.h.; ISO 527-1, ISO 527-3; Sample type 2 | ||
| Film Elongation at Break, TD | 170 % | 170 % | Test speed 100%/min.; 50% r.h.; ISO 527-1, ISO 527-3; Sample type 2 | ||
| Electrical Properties | Metric | English | Comments | ||
| Dielectric Constant | 3.3 @Frequency 50.0 Hz, Temperature 23.0 °C | 3.3 @Frequency 50.0 Hz, Temperature 73.4 °F | DIN 40634 or VDE 0345 in air or ASTM D150 | ||
| 3.3 @Frequency 1000 Hz, Temperature 23.0 °C | 3.3 @Frequency 1000 Hz, Temperature 73.4 °F | DIN 40634 or VDE 0345 in air or ASTM D150 | |||
| 3.6 @Frequency 50.0 Hz, Temperature 150 °C | 3.6 @Frequency 50.0 Hz, Temperature 302 °F | DIN 40634 or VDE 0345 in air or ASTM D150 | |||
| Dissipation Factor | 0.0020 @Frequency 50.0 Hz, Temperature 23.0 °C | 0.0020 @Frequency 50.0 Hz, Temperature 73.4 °F | tand; DIN 40634 or VDE 0345 in air or ASTM D149 | ||
| 0.0048 @Frequency 50.0 Hz, Temperature 150 °C | 0.0048 @Frequency 50.0 Hz, Temperature 302 °F | tand; DIN 40634 or VDE 0345 in air or ASTM D149 | |||
| 0.0052 @Frequency 1000 Hz, Temperature 23.0 °C | 0.0052 @Frequency 1000 Hz, Temperature 73.4 °F | tand; DIN 40634 or VDE 0345 in air or ASTM D149 | |||
| Descriptive Properties | |||||
| Behavior Under the Influence of Partial Discharges (Min.) | 900 | DIN 53485 or VDE 0303/part 7; Contact method, 40KV/mm | |||
| Conductivity of Aqueous Extract (μS/cm) | 2 | DIN 40634 or VDE 0345; 1 kHz | |||
| Frigen Extract (%) | 0.05 | DIN 8944; Cold extraction | |||
| Insulation Class in Electrical Engineering | B | DIN 57530 or VDE 0530, main list | |||
| Trichloroethylene- Extract (%) | 0.2 | DIN 8943; Extracted in Soxhalet apparatus for 2h. Boiled down for 15h at 105oC | |||