Mitsubishi Hostaphan? RN, 50 micron Nominal Thickness Universal Polyethylene Terephthalate Film

Mitsubishi Hostaphan? RN, 50 micron Nominal Thickness Universal Polyethylene Terephthalate Film 物性表: Mitsubishi Hostaphan? RN, 50 micron Nominal Thickness Universal Polyethylene Terephthalate Film物性表及特性介紹,Mitsubishi Hostaphan? RN, 50 micron Nominal Thickness Universal Polyethylene Terephthalate Film注塑參數(shù)詳情,如需Mitsubishi Hostaphan? RN, 50 micron Nominal Thickness Universal Polyethylene Terephthalate Film下載, 可到相關(guān)下載區(qū)下載

密度 [g/cm3]: 1.4
吸水率 [%]: 0.5

Physical Properties	Metric	English	Comments

Density	1.40 g/cc @Temperature 23.0 °C	0.0506 lb/in3 @Temperature 73.4 °F	ASTM D1505-68, method C
Water Absorption	0.50 % @Temperature 23.0 °C	0.50 % @Temperature 73.4 °F	4 days in water; ASTM D570
Linear Mold Shrinkage	0.010 cm/cm @Temperature 150 °C, Time 900 sec	0.010 in/in @Temperature 302 °F, Time 0.250 hour	DIN 40634
Linear Mold Shrinkage, Transverse	0.0030 cm/cm @Temperature 150 °C, Time 900 sec	0.0030 in/in @Temperature 302 °F, Time 0.250 hour	DIN 40634

Mechanical Properties	Metric	English	Comments
Film Tensile Strength at Yield, MD	210 MPa	30500 psi	Test speed 100%/min.; 50% r.h.; ISO 527-1, ISO 527-3; Sample type 2
Film Tensile Strength at Yield, TD	260 MPa	37700 psi	Test speed 100%/min.; 50% r.h.; ISO 527-1, ISO 527-3; Sample type 2
Film Elongation at Break, MD	>= 150 %	>= 150 %	Test speed 100%/min.; 50% r.h.; ISO 527-1, ISO 527-3; Sample type 2
Film Elongation at Break, TD	110 %	110 %	Test speed 100%/min.; 50% r.h.; ISO 527-1, ISO 527-3; Sample type 2
Modulus of Elasticity	4.00 GPa @Temperature 23.0 °C	580 ksi @Temperature 73.4 °F	MD; Test speed 1%/min.; 50% r.h.; ISO 527-1, ISO 527-3; Sample type 2
	5.20 GPa @Temperature 23.0 °C	754 ksi @Temperature 73.4 °F	TD; Test speed 1%/min.; 50% r.h.; ISO 527-1, ISO 527-3; Sample type 2
Coefficient of Friction, Static	0.40	0.40	DIN 53375 or ASTM D1894

Electrical Properties	Metric	English	Comments
Dielectric Constant	2.9 @Frequency 2.40e+8 Hz, Temperature 23.0 °C	2.9 @Frequency 2.40e+8 Hz, Temperature 73.4 °F	DIN 40634 or VDE 0345 in air
	2.9 @Frequency 9.30e+9 Hz, Temperature 23.0 °C	2.9 @Frequency 9.30e+9 Hz, Temperature 73.4 °F	DIN 40634 or VDE 0345 in air
	3.2 @Frequency 1.00e+6 Hz, Temperature 23.0 °C	3.2 @Frequency 1.00e+6 Hz, Temperature 73.4 °F	DIN 40634 or VDE 0345 in air
	3.3 @Frequency 50.0 Hz, Temperature 23.0 °C	3.3 @Frequency 50.0 Hz, Temperature 73.4 °F	DIN 40634 or VDE 0345 in air
	3.3 @Frequency 1000 Hz, Temperature 23.0 °C	3.3 @Frequency 1000 Hz, Temperature 73.4 °F	DIN 40634 or VDE 0345 in air
	3.6 @Frequency 50.0 Hz, Temperature 150 °C	3.6 @Frequency 50.0 Hz, Temperature 302 °F	DIN 40634 or VDE 0345 in air

Optical Properties	Metric	English	Comments
Haze	13 %	13 %	Enlarged measurement angle; ASTM D1003-61, method A

Descriptive Properties
Conductivity of Aqueous Extract (μS/cm)	2		DIN 40634 or VDE 0345; 1 kHz
F5-value (MPa)	105		ISO 527-1, ISO 527-3; Sample type 2; MD; Test speed 100%/min.; 23oC, 50% r.h.
	105		ISO 527-1, ISO 527-3; Sample type 2; TD; Test speed 100%/min.; 23oC, 50% r.h.

關(guān)鍵詞:
PET
供應(yīng)
Mitsubishi Hostaphan? RN
50 micron Nominal Thickness Universal Polyethylene Terephthalate Film

轉(zhuǎn)載請(qǐng)注明: 轉(zhuǎn)自中國(guó)塑膠原料之家 http://www.spnmy.cn/wuxingbiao/

本文鏈接: http://www.spnmy.cn/yuanliaoku/show-39289.html

免責(zé)聲明: 本文 Mitsubishi Hostaphan? RN, 50 micron Nominal Thickness Universal Polyethylene Terephthalate Film 僅代表作者個(gè)人觀點(diǎn)，中國(guó)塑膠原料之家無關(guān)。中國(guó)塑膠原料之家網(wǎng)所轉(zhuǎn)載的內(nèi)容，其版權(quán)均由原作者和資料提供方所擁有！如因作品版權(quán)問題需要處理，請(qǐng)與我們聯(lián)絡(luò)