- 密度 [g/cm3]: 1.68
- 缺口沖擊強(qiáng)度: 0.9
- 彎曲模量 [MPa]: 14.0
| Physical Properties | Metric | English | Comments |
|---|---|---|---|
| Density | 1.68 g/cc | 0.0607 lb/in3 | ASTM D792 |
| Linear Mold Shrinkage, Flow | 0.0040 cm/cm @Thickness 2.00 mm | 0.0040 in/in @Thickness 0.0787 in | ASTM D955 |
| Linear Mold Shrinkage, Transverse | 0.010 cm/cm @Thickness 2.00 mm | 0.010 in/in @Thickness 0.0787 in | ASTM D955 |
| Ash | 45 % | 45 % | ASTM D2854 |
| Mechanical Properties | Metric | English | Comments |
| Tensile Strength at Break | 160 MPa | 23200 psi | 5 mm/min; ASTM D638 |
| Flexural Strength | 240 MPa | 34800 psi | 1.3 mm/min; ASTM D790 |
| Flexural Modulus | 14.0 GPa | 2030 ksi | 1.3 mm/min; ASTM D790 |
| Izod Impact, Notched | 0.900 J/cm @Temperature 23.0 °C | 1.69 ft-lb/in @Temperature 73.4 °F | ASTM D256 |
| Thermal Properties | Metric | English | Comments |
| Deflection Temperature at 1.8 MPa (264 psi) | 230 °C | 446 °F | ASTM D648 |
| Processing Properties | Metric | English | Comments |
| Feed Temperature | 260 - 270 °C | 500 - 518 °F | |
| Middle Barrel Temperature | 265 - 275 °C | 509 - 527 °F | |
| Front Barrel Temperature | 270 - 295 °C | 518 - 563 °F | |
| Nozzle Temperature | 275 - 300 °C | 527 - 572 °F | |
| Melt Temperature | 275 - 300 °C | 527 - 572 °F | |
| Mold Temperature | 95.0 - 120 °C | 203 - 248 °F | |
| Injection Pressure | 55.0 - 85.0 MPa | 7980 - 12300 psi | |