- 密度 [g/cm3]: 1.65
- 缺口沖擊強(qiáng)度: 0.9
- 彎曲模量 [MPa]: 10.2
| Physical Properties | Metric | English | Comments |
|---|---|---|---|
| Density | 1.65 g/cc | 0.0596 lb/in3 | ASTM D792 |
| Linear Mold Shrinkage, Flow | 0.0020 cm/cm @Thickness 2.00 mm | 0.0020 in/in @Thickness 0.0787 in | ASTM D955 |
| Linear Mold Shrinkage, Transverse | 0.0090 cm/cm @Thickness 2.00 mm | 0.0090 in/in @Thickness 0.0787 in | ASTM D955 |
| Mechanical Properties | Metric | English | Comments |
| Tensile Strength at Break | 145 MPa | 21000 psi | 5 mm/min; ASTM D638 |
| Flexural Strength | 215 MPa | 31200 psi | 1.3 mm/min; ASTM D790 |
| Flexural Modulus | 10.2 GPa | 1480 ksi | 1.3 mm/min; ASTM D790 |
| Izod Impact, Notched | 0.900 J/cm @Temperature 23.0 °C | 1.69 ft-lb/in @Temperature 73.4 °F | ASTM D256 |
| Electrical Properties | Metric | English | Comments |
| Volume Resistivity | 1.00e+16 ohm-cm | 1.00e+16 ohm-cm | ASTM D257 |
| Dielectric Strength | 29.0 kV/mm | 737 kV/in | ASTM D149 |
| Comparative Tracking Index | 15 - 30 V | 15 - 30 V | UL746 |
| Thermal Properties | Metric | English | Comments |
| Deflection Temperature at 1.8 MPa (264 psi) | 228 °C | 442 °F | ASTM D648 |
| Flammability, UL94 | V-0 @Thickness 0.850 mm | V-0 @Thickness 0.0335 in | |
| 5VA @Thickness 1.50 mm | 5VA @Thickness 0.0591 in | ||
| 5VA @Thickness 3.00 mm | 5VA @Thickness 0.118 in | ||
| Glow Wire Test | 825 °C | 1520 °F | GWIT at 1.0 mm; IEC 60695-2-13 |
| 960 °C | 1760 °F | GWFI at 1.0 mm; IEC 60695-2-13 | |
| Processing Properties | Metric | English | Comments |
| Feed Temperature | 260 - 270 °C | 500 - 518 °F | |
| Middle Barrel Temperature | 265 - 275 °C | 509 - 527 °F | |
| Front Barrel Temperature | 270 - 290 °C | 518 - 554 °F | |
| Nozzle Temperature | 275 - 295 °C | 527 - 563 °F | |
| Melt Temperature | 275 - 295 °C | 527 - 563 °F | |
| Mold Temperature | 95.0 - 120 °C | 203 - 248 °F | |
| Injection Pressure | 55.0 - 85.0 MPa | 7980 - 12300 psi | |